Y3Zn11: enthalpy of formation
3 accepted literature formation-enthalpy value(s) (experimental 1, model 2); experimental median -40 kJ/mol-atom (n = 1); Materials Project -33.683 kJ/mol-atom (mp-aaackuls); OQMD -33.029 kJ/mol-atom (oqmd-1454495).
Systems: Y–Zn
Literature values
| Value | Phase as printed | T (K) | Class | Method | System | Source | Location | Quote |
|---|---|---|---|---|---|---|---|---|
| -40 kJ/mol-atom ± 2 | Y3Zn11 | 298.15 | experimental | Y–Zn | [1] Shao 2006 cites Mason 1976 doi | Table 2, p. 4, row 14 report | ||
| -38.743 kJ/mol-atom | Y3Zn11 | model | CALPHAD | Y–Zn | [1] Shao 2006 | Table 2, p. 4, row 13 report | ||
| -36 kJ/mol-atom | Y3Zn11 | model | Y–Zn | [1] Shao 2006 cites F 1988 | Table 2, p. 4, row 15 report |
Uncertainty budget
Components kept separate, in the value's unit (literature SCHEMA.md, UNCERTAINTY_CALIBRATION.md): effective = max(sqrt(max(printed, reading, method)^2 + composition^2 + conversion^2), scatter). The method floor is the robust between-study scatter of the method class in ORCHID (calibrated) or a documented prior; printed values and printed uncertainties are unchanged.
| Value | Unit | Printed | Reading | Method (class, basis) | Composition | Scatter | Conversion | Effective |
|---|---|---|---|---|---|---|---|---|
| -40 | kJ/mol-atom | 2 | 0.5 | 3.5 (unknown, calibrated) | 3.5 | |||
| -38.743 | kJ/mol-atom | 5.000e-4 | 3.9 (model_calculated, calibrated) | 3.9 | ||||
| -36 | kJ/mol-atom | 0.5 | 3.9 (model_calculated, calibrated) | 3.9 |
DFT formation energies
Lowest-energy entries at this composition. Materials Project and OQMD use different energy references and are never averaged. 1 eV/atom = 96.485 kJ/mol-atom.
| Source | Entry | kJ/mol-atom | eV/atom | Space group | E above hull (kJ/mol-atom) | E above hull (eV/atom) | Theoretical |
|---|---|---|---|---|---|---|---|
| Materials Project | mp-aaackuls | -33.683 | -0.349104 | Immm | 0 | 0 | no |
| OQMD | oqmd-1454495 | -33.029 | -0.342321 | Immm | 0 | 0 | yes |
DFT sources: A. Jain et al., Commentary: The Materials Project: A materials genome approach to accelerating materials innovation, APL Materials 1 (2013) 011002. doi:10.1063/1.4812323 (CC BY 4.0); J. E. Saal et al., JOM 65 (2013) 1501-1509; S. Kirklin et al., npj Comput. Mater. 1 (2015) 15010. doi:10.1007/s11837-013-0755-4 (CC BY 4.0);
Sources
- G. Shao, V. Varsani, Z. Fan, Thermodynamic modelling of the Y–Zn and Mg–Zn–Y systems, Calphad 30, 286-295 (2006). doi:10.1016/j.calphad.2006.03.005