Au–Ge–Sb system
7 accepted literature values from 1 paper(s) (experimental 2, model 5); 0 calculated phase diagram(s). 2 further extracted value(s) not accepted by the reader-agreement checks are only in the JSON/CSV.
Data: JSON · CSV · interactive explorer · papers (bibliography) · Markdown
| Evidence class | Values |
|---|---|
| experimental | 2 |
| model | 5 |
| Property group | Values |
|---|---|
| invariant reaction | 7 |
Invariant reactions (literature)
| T (K) | Reaction / phases | Compositions (mole fraction) | Class | Source | Location | Quote |
|---|---|---|---|---|---|---|
| 740 | peritectic: L + (Sb) -> AuSb2 | L: Sb 0.655 | model | [1] Wang 2009 cites Liu 2003 doi | Table 1, p. 2, row 7 report | |
| 703 | quasi-peritectic: L+(Sb) -> (Ge)+AuSb2 | L: Ge 0.14, Sb 0.51 | experimental | [1] Wang 2009 cites Zwingmann 1964 | Table 1, p. 2, row 9 report | |
| 702 | quasi-peritectic: L+(Sb) -> (Ge)+AuSb2 | L: Ge 0.137, Sb 0.487 | model | [1] Wang 2009 | Table 1, p. 2, row 10 report | |
| 631 | eutectic: L -> (Au) + (Ge) | L: Ge 0.294 | model | [1] Wang 2009 cites Wang 2009 doi | Table 1, p. 2, row 6 report | |
| 626 | eutectic: L -> (Au) + AuSb2 | L: Sb 0.366 | model | [1] Wang 2009 cites Liu 2003 doi | Table 1, p. 2, row 8 report | |
| 561 | eutectic: L -> (Au) + (Ge) + AuSb2 | L: Ge 0.15, Sb 0.17 | experimental | [1] Wang 2009 cites Zwingmann 1964 | Table 1, p. 2, row 11 report | |
| 560 | eutectic: L -> (Au) + (Ge) + AuSb2 | L: Ge 0.166, Sb 0.195 | model | [1] Wang 2009 | Table 1, p. 2, row 12 report |