Fe–Ni–W system

118 accepted literature values from 1 paper(s) (experimental 118); 0 calculated phase diagram(s). 4 further extracted value(s) not accepted by the reader-agreement checks are only in the JSON/CSV.

Data: JSON · CSV · interactive explorer · papers (bibliography) · Markdown

Accepted values by evidence class
Evidence class	Values
experimental	118

Accepted values by property group
Property group	Values
phase equilibrium	118

Other properties

Phase equilibrium (118)

Phase equilibrium, Fe–Ni–W system
Property	T (K)	Phases / composition	Class	Source	Location
Phase composition	1273	"Ni4W" + "NiW" "Ni4W": Fe 0.001476, Ni 0.808876, W 0.189648; "NiW": Fe 0.004183, Ni 0.531361, W 0.464456	experimental	[1] Guillermet 1986	Table IV, p. 3, row 11 report
Phase composition	1273	"Ni4W" + "NiW" "Ni4W": Fe 0.021949, Ni 0.793585, W 0.184466; "NiW": Fe 0, Ni 0.517397, W 0.482603	experimental	[1] Guillermet 1986	Table V, p. 3, row 4 report
Phase composition	1273	bcc + Laves bcc: Fe 0.966707, Ni 0.002039, W 0.031254; Laves: Fe 0.685316, Ni 0.001634, W 0.31305	experimental	[1] Guillermet 1986	Table IV, p. 3, row 22 report
Phase composition	1273	bcc + Laves bcc: Fe 0.972282, Ni 0.004013, W 0.023705; Laves: Fe 0.690666, Ni 0.001623, W 0.307712	experimental	[1] Guillermet 1986	Table V, p. 3, row 9 report
Phase composition	1273	bcc(W) + fcc fcc: Fe 0.112257, Ni 0.757837, W 0.129906	experimental	[1] Guillermet 1986	Table V, p. 3, row 13 report
Phase composition	1273	bcc(W) + fcc fcc: Fe 0.248505, Ni 0.668569, W 0.082926	experimental	[1] Guillermet 1986	Table V, p. 3, row 14 report
Phase composition	1273	bcc(W) + fcc fcc: Fe 0.440083, Ni 0.515355, W 0.044561	experimental	[1] Guillermet 1986	Table V, p. 3, row 15 report
Phase composition	1273	bcc(W) + fcc bcc(W): Fe 0.030956, Ni 0.055962, W 0.913082; fcc: Fe 0.335068, Ni 0.608933, W 0.055999	experimental	[1] Guillermet 1986	Table V, p. 3, row 1 report
Phase composition	1273	bcc(W) + fcc bcc(W): Fe 0.031018, Ni 0.053123, W 0.915858; fcc: Fe 0.323561, Ni 0.616828, W 0.059611	experimental	[1] Guillermet 1986	Table V, p. 3, row 6 report
Phase composition	1273	bcc(W) + μ-Phase μ-Phase: Fe 0.453762, Ni 0.132127, W 0.414111	experimental	[1] Guillermet 1986	Table IV, p. 3, row 16 report
Phase composition	1273	fcc + "Ni4W" fcc: Fe 0, Ni 0.853307, W 0.146693; "Ni4W": Fe 0, Ni 0.812222, W 0.187778	experimental	[1] Guillermet 1986	Table IV, p. 3, row 5 report
Phase composition	1273	fcc + "Ni4W" fcc: Fe 0.008283, Ni 0.844533, W 0.147184; "Ni4W": Fe 0, Ni 0.810967, W 0.189033	experimental	[1] Guillermet 1986	Table IV, p. 3, row 12 report
Phase composition	1273	fcc + "Ni4W" fcc: Fe 0.005669, Ni 0.830721, W 0.163609; "Ni4W": Fe 0, Ni 0.811595, W 0.188405	experimental	[1] Guillermet 1986	Table V, p. 3, row 2 report
Phase composition	1273	fcc + "NiW" fcc: Fe 0.039758, Ni 0.816566, W 0.143676; "NiW": Fe 0.018939, Ni 0.510575, W 0.470486	experimental	[1] Guillermet 1986	Table V, p. 3, row 3 report
Phase composition	1273	fcc + "NiW" fcc: Fe 0.097289, Ni 0.77478, W 0.12793; "NiW": Fe 0.048663, Ni 0.475091, W 0.476247	experimental	[1] Guillermet 1986	Table IV, p. 3, row 7 report
Phase composition	1273	fcc + Laves fcc: Fe 0.964137, Ni 0.018802, W 0.017061; Laves: Fe 0.688257, Ni 0.004863, W 0.30688	experimental	[1] Guillermet 1986	Table IV, p. 3, row 8 report
Phase composition	1273	fcc + Laves fcc: Fe 0.967111, Ni 0.015831, W 0.017058; Laves: Fe 0.684554, Ni 0.003265, W 0.312181	experimental	[1] Guillermet 1986	Table V, p. 3, row 10 report
Phase composition	1273	fcc + μ-Phase fcc: Fe 0.876704, Ni 0.096405, W 0.026891; μ-Phase: Fe 0.609708, Ni 0.015918, W 0.374374	experimental	[1] Guillermet 1986	Table IV, p. 3, row 19 report
Phase composition	1273	fcc + μ-Phase fcc: Fe 0.874662, Ni 0.098445, W 0.026894; μ-Phase: Fe 0.617022, Ni 0.020905, W 0.362073	experimental	[1] Guillermet 1986	Table V, p. 3, row 20 report
Phase composition	1273	fcc + μ-Phase fcc: Fe 0.88194, Ni 0.083502, W 0.034558; μ-Phase: Fe 0.622349, Ni 0.015674, W 0.361977	experimental	[1] Guillermet 1986	Table V, p. 3, row 18 report
Phase composition	1273	fcc + μ-Phase fcc: Fe 0.581045, Ni 0.384589, W 0.034367; μ-Phase: Fe 0.474991, Ni 0.118058, W 0.406951	experimental	[1] Guillermet 1986	Table IV, p. 3, row 17 report
Phase composition	1273	μ-Phase + Laves μ-Phase: Fe 0.61024, Ni 0.001798, W 0.387962; Laves: Fe 0.683516, Ni 0.001638, W 0.314846	experimental	[1] Guillermet 1986	Table IV, p. 3, row 21 report
Phase composition	1473	bcc + fcc bcc: Fe 0.907306, Ni 0.030481, W 0.062213; fcc: Fe 0.914804, Ni 0.040948, W 0.044248	experimental	[1] Guillermet 1986	Table VI, p. 4, row 9 report
Phase composition	1473	bcc + fcc bcc: Fe 0.941685, Ni 0.016689, W 0.041626; fcc: Fe 0.948303, Ni 0.020414, W 0.031283	experimental	[1] Guillermet 1986	Table VI, p. 4, row 27 report
Phase composition	1473	bcc + fcc bcc: Fe 0.951104, Ni 0.012081, W 0.036816; fcc: Fe 0.959867, Ni 0.016075, W 0.024058	experimental	[1] Guillermet 1986	Table VI, p. 4, row 10 report
Phase composition	1473	bcc + μ-Phase bcc: Fe 0.916384, Ni 0.026911, W 0.056705; μ-Phase: Fe 0.605443, Ni 0.010734, W 0.383823	experimental	[1] Guillermet 1986	Table VI, p. 4, row 16 report
Phase composition	1473	bcc + μ-Phase bcc: Fe 0.919251, Ni 0.029793, W 0.050956; μ-Phase: Fe 0.590664, Ni 0.009123, W 0.400213	experimental	[1] Guillermet 1986	Table VI, p. 4, row 18 report
Phase composition	1473	bcc + μ-Phase bcc: Fe 0.916384, Ni 0.026911, W 0.056705; μ-Phase: Fe 0.597759, Ni 0.010833, W 0.391408	experimental	[1] Guillermet 1986	Table VI, p. 4, row 17 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.216614, Ni 0.682184, W 0.101202	experimental	[1] Guillermet 1986	Table VI, p. 4, row 6 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.273063, Ni 0.638359, W 0.088578	experimental	[1] Guillermet 1986	Table VI, p. 4, row 5 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.42397, Ni 0.509846, W 0.066183	experimental	[1] Guillermet 1986	Table VI, p. 4, row 30 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.404342, Ni 0.52941, W 0.066248	experimental	[1] Guillermet 1986	Table VI, p. 4, row 31 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.284497, Ni 0.633161, W 0.082342	experimental	[1] Guillermet 1986	Table VI, p. 4, row 34 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.281552, Ni 0.63478, W 0.083668	experimental	[1] Guillermet 1986	Table VI, p. 4, row 32 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.056718, Ni 0.793683, W 0.149599	experimental	[1] Guillermet 1986	Table VI, p. 4, row 8 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.248223, Ni 0.661294, W 0.090483	experimental	[1] Guillermet 1986	Table VI, p. 4, row 29 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.492522, Ni 0.439472, W 0.068006	experimental	[1] Guillermet 1986	Table VI, p. 4, row 20 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.500581, Ni 0.435113, W 0.064306	experimental	[1] Guillermet 1986	Table VI, p. 4, row 1 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.309753, Ni 0.608007, W 0.082239	experimental	[1] Guillermet 1986	Table VI, p. 4, row 4 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.367357, Ni 0.555809, W 0.076834	experimental	[1] Guillermet 1986	Table VI, p. 4, row 3 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.110928, Ni 0.759158, W 0.129914	experimental	[1] Guillermet 1986	Table VI, p. 4, row 7 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.495986, Ni 0.437249, W 0.066764	experimental	[1] Guillermet 1986	Table VI, p. 4, row 11 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.433705, Ni 0.495188, W 0.071107	experimental	[1] Guillermet 1986	Table VI, p. 4, row 2 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.418201, Ni 0.515596, W 0.066202	experimental	[1] Guillermet 1986	Table VI, p. 4, row 28 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.392305, Ni 0.537277, W 0.070419	experimental	[1] Guillermet 1986	Table VI, p. 4, row 19 report
Phase composition	1473	bcc(W) + fcc fcc: Fe 0.270544, Ni 0.643537, W 0.085919	experimental	[1] Guillermet 1986	Table VI, p. 4, row 33 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.916434, Ni 0.043702, W 0.039864; μ-Phase: Fe 0.592183, Ni 0.010905, W 0.396912	experimental	[1] Guillermet 1986	Table VI, p. 4, row 15 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.635287, Ni 0.313022, W 0.051691; μ-Phase: Fe 0.477389, Ni 0.111238, W 0.411373	experimental	[1] Guillermet 1986	Table VI, p. 4, row 26 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.857418, Ni 0.097095, W 0.045487; μ-Phase: Fe 0.594834, Ni 0.017967, W 0.387198	experimental	[1] Guillermet 1986	Table VI, p. 4, row 23 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.60386, Ni 0.336164, W 0.059976; μ-Phase: Fe 0.474674, Ni 0.108244, W 0.417083	experimental	[1] Guillermet 1986	Table VI, p. 4, row 12 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.925075, Ni 0.031435, W 0.04349; μ-Phase: Fe 0.584981, Ni 0.009185, W 0.405835	experimental	[1] Guillermet 1986	Table VI, p. 4, row 14 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.814533, Ni 0.138014, W 0.047452; μ-Phase: Fe 0.564774, Ni 0.039939, W 0.395286	experimental	[1] Guillermet 1986	Table VI, p. 4, row 25 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.611246, Ni 0.329197, W 0.059557; μ-Phase: Fe 0.467868, Ni 0.120565, W 0.411567	experimental	[1] Guillermet 1986	Table VI, p. 4, row 21 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.730422, Ni 0.215831, W 0.053747; μ-Phase: Fe 0.528187, Ni 0.055839, W 0.415974	experimental	[1] Guillermet 1986	Table VI, p. 4, row 13 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.636809, Ni 0.305681, W 0.05751; μ-Phase: Fe 0.503348, Ni 0.100154, W 0.396498	experimental	[1] Guillermet 1986	Table VI, p. 4, row 22 report
Phase composition	1473	fcc + μ-Phase fcc: Fe 0.882486, Ni 0.073562, W 0.043952; μ-Phase: Fe 0.594834, Ni 0.017967, W 0.387198	experimental	[1] Guillermet 1986	Table VI, p. 4, row 24 report
Phase composition	1573	bcc + fcc bcc: Fe 0.864158, Ni 0.048096, W 0.087745; fcc: Fe 0.867618, Ni 0.075537, W 0.056845	experimental	[1] Guillermet 1986	Table VII, p. 5, row 8 report
Phase composition	1573	bcc + fcc bcc: Fe 0.865433, Ni 0.061284, W 0.073283; fcc: Fe 0.86526, Ni 0.078663, W 0.056077	experimental	[1] Guillermet 1986	Table VII, p. 5, row 13 report
Phase composition	1573	bcc + fcc bcc: Fe 0.870122, Ni 0.048633, W 0.081245; fcc: Fe 0.872212, Ni 0.072117, W 0.055671	experimental	[1] Guillermet 1986	Table VII, p. 5, row 33 report
Phase composition	1573	bcc + fcc bcc: Fe 0.864604, Ni 0.05836, W 0.077036; fcc: Fe 0.866531, Ni 0.07662, W 0.056849	experimental	[1] Guillermet 1986	Table VII, p. 5, row 30 report
Phase composition	1573	bcc + μ-Phase bcc: Fe 0.862247, Ni 0.0586, W 0.079153; μ-Phase: Fe 0.594864, Ni 0.023211, W 0.381925	experimental	[1] Guillermet 1986	Table VII, p. 5, row 14 report
Phase composition	1573	bcc + μ-Phase bcc: Fe 0.868213, Ni 0.060986, W 0.070802; μ-Phase: Fe 0.587159, Ni 0.025149, W 0.387692	experimental	[1] Guillermet 1986	Table VII, p. 5, row 31 report
Phase composition	1573	bcc + μ-Phase bcc: Fe 0.865458, Ni 0.056247, W 0.078295; μ-Phase: Fe 0.55525, Ni 0.022481, W 0.422269	experimental	[1] Guillermet 1986	Table VII, p. 5, row 2 report
Phase composition	1573	bcc + μ-Phase bcc: Fe 0.86992, Ni 0.056814, W 0.073266; μ-Phase: Fe 0.591938, Ni 0.025032, W 0.38303	experimental	[1] Guillermet 1986	Table VII, p. 5, row 7 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.547372, Ni 0.382749, W 0.069879	experimental	[1] Guillermet 1986	Table VII, p. 5, row 10 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.298348, Ni 0.609135, W 0.092517	experimental	[1] Guillermet 1986	Table VII, p. 5, row 22 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.507526, Ni 0.418283, W 0.07419	experimental	[1] Guillermet 1986	Table VII, p. 5, row 17 report
Phase composition	1573	bcc(W) + fcc bcc(W): Fe 0.015459, Ni 0.073542, W 0.910999; fcc: Fe 0.189742, Ni 0.691008, W 0.119251	experimental	[1] Guillermet 1986	Table VII, p. 5, row 27 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.332364, Ni 0.579762, W 0.087874	experimental	[1] Guillermet 1986	Table VII, p. 5, row 20 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.580469, Ni 0.34561, W 0.073921	experimental	[1] Guillermet 1986	Table VII, p. 5, row 18 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.189274, Ni 0.696917, W 0.11381	experimental	[1] Guillermet 1986	Table VII, p. 5, row 26 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.206548, Ni 0.681692, W 0.111761	experimental	[1] Guillermet 1986	Table VII, p. 5, row 24 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.384239, Ni 0.535125, W 0.080636	experimental	[1] Guillermet 1986	Table VII, p. 5, row 16 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.603515, Ni 0.32265, W 0.073836	experimental	[1] Guillermet 1986	Table VII, p. 5, row 11 report
Phase composition	1573	bcc(W) + fcc bcc(W): Fe 0.024723, Ni 0.064688, W 0.910589; fcc: Fe 0.190545, Ni 0.683643, W 0.125812	experimental	[1] Guillermet 1986	Table VII, p. 5, row 1 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.533957, Ni 0.389841, W 0.076201	experimental	[1] Guillermet 1986	Table VII, p. 5, row 19 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.335741, Ni 0.580814, W 0.083445	experimental	[1] Guillermet 1986	Table VII, p. 5, row 9 report
Phase composition	1573	bcc(W) + fcc bcc(W): Fe 0.018965, Ni 0.039097, W 0.941937; fcc: Fe 0.27153, Ni 0.630332, W 0.098139	experimental	[1] Guillermet 1986	Table VII, p. 5, row 21 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.614546, Ni 0.312077, W 0.073377	experimental	[1] Guillermet 1986	Table VII, p. 5, row 4 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.267807, Ni 0.634036, W 0.098157	experimental	[1] Guillermet 1986	Table VII, p. 5, row 23 report
Phase composition	1573	bcc(W) + fcc fcc: Fe 0.230463, Ni 0.665105, W 0.104431	experimental	[1] Guillermet 1986	Table VII, p. 5, row 25 report
Phase composition	1573	bcc(W) + μ-Phase μ-Phase: Fe 0.471677, Ni 0.116833, W 0.41149	experimental	[1] Guillermet 1986	Table VII, p. 5, row 3 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.862184, Ni 0.080955, W 0.056861; μ-Phase: Fe 0.583417, Ni 0.027034, W 0.389548	experimental	[1] Guillermet 1986	Table VII, p. 5, row 28 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.64758, Ni 0.284121, W 0.068299; μ-Phase: Fe 0.491324, Ni 0.096464, W 0.412212	experimental	[1] Guillermet 1986	Table VII, p. 5, row 12 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.859908, Ni 0.081276, W 0.058816; μ-Phase: Fe 0.585661, Ni 0.026963, W 0.387376	experimental	[1] Guillermet 1986	Table VII, p. 5, row 29 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.844931, Ni 0.09738, W 0.057689; μ-Phase: Fe 0.585977, Ni 0.023456, W 0.390567	experimental	[1] Guillermet 1986	Table VII, p. 5, row 15 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.863636, Ni 0.07795, W 0.058414; μ-Phase: Fe 0.597782, Ni 0.021396, W 0.380822	experimental	[1] Guillermet 1986	Table VII, p. 5, row 6 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.871768, Ni 0.072174, W 0.056059; μ-Phase: Fe 0.598149, Ni 0.023121, W 0.37873	experimental	[1] Guillermet 1986	Table VII, p. 5, row 32 report
Phase composition	1573	fcc + μ-Phase fcc: Fe 0.618666, Ni 0.30839, W 0.072945; μ-Phase: Fe 0.472274, Ni 0.115124, W 0.412603	experimental	[1] Guillermet 1986	Table VII, p. 5, row 5 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.511273, Ni 0.398968, W 0.089759	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 11 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.031206, Ni 0.044538, W 0.924256; fcc: Fe 0.181716, Ni 0.703941, W 0.114343	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 3 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.632543, Ni 0.281322, W 0.086135	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 16 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.040632, Ni 0.032712, W 0.926656; fcc: Fe 0.462402, Ni 0.445828, W 0.09177	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 10 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.043313, Ni 0.044154, W 0.912533; fcc: Fe 0.50727, Ni 0.40473, W 0.088	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 12 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.326762, Ni 0.573977, W 0.09926	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 9 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.040632, Ni 0.032712, W 0.926656; fcc: Fe 0.45747, Ni 0.449386, W 0.093144	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 7 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.009565, Ni 0.036405, W 0.95403; fcc: Fe 0.094451, Ni 0.77029, W 0.135259	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 4 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.062318, Ni 0.014824, W 0.922858; fcc: Fe 0.640593, Ni 0.27243, W 0.086977	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 1 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.329667, Ni 0.572475, W 0.097858	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 15 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.207573, Ni 0.666719, W 0.125707	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 8 report
Phase composition	1673	bcc(W) + fcc fcc: Fe 0.156294, Ni 0.713041, W 0.130664	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 14 report
Phase composition	1673	bcc(W) + fcc bcc(W): Fe 0.033978, Ni 0.055842, W 0.91018; fcc: Fe 0.10532, Ni 0.750918, W 0.143761	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 13 report
Phase composition	1673	bcc(W) + μ-Phase μ-Phase: Fe 0.46853, Ni 0.103892, W 0.427578	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 18 report
Phase composition	1673	bcc(W) + μ-Phase bcc(W): Fe 0.077062, Ni 0.014664, W 0.908273; μ-Phase: Fe 0.489751, Ni 0.076079, W 0.43417	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 2 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.802348, Ni 0.119529, W 0.078123; μ-Phase: Fe 0.569127, Ni 0.043177, W 0.387696	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 19 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.636186, Ni 0.27239, W 0.091424; μ-Phase: Fe 0.492023, Ni 0.10137, W 0.406607	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 17 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.922753, Ni 0.00989, W 0.067357; μ-Phase: Fe 0.610579, Ni 0.003586, W 0.385835	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 22 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.932497, Ni 0.002188, W 0.065315; μ-Phase: Fe 0.616709, Ni 0.001784, W 0.381508	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 24 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.767793, Ni 0.148389, W 0.083818; μ-Phase: Fe 0.531554, Ni 0.046829, W 0.421616	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 6 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.860396, Ni 0.068775, W 0.07083; μ-Phase: Fe 0.583417, Ni 0.027034, W 0.389548	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 21 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.82451, Ni 0.099886, W 0.075604; μ-Phase: Fe 0.567783, Ni 0.03807, W 0.394147	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 20 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.934506, Ni 0.002179, W 0.063315; μ-Phase: Fe 0.613817, Ni 0.003572, W 0.382611	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 25 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.735947, Ni 0.177928, W 0.086125; μ-Phase: Fe 0.531554, Ni 0.046829, W 0.421616	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 5 report
Phase composition	1673	fcc + μ-Phase fcc: Fe 0.933302, Ni 0.002185, W 0.064513; μ-Phase: Fe 0.61489, Ni 0.003567, W 0.381542	experimental	[1] Guillermet 1986	Table VIII, p. 6, row 23 report
Phase composition	1673	γ + μ + W + fcc fcc: Fe 0.642961, Ni 0.274816, W 0.082223; μ: Fe 0.528311, Ni 0.096204, W 0.375485	experimental	[1] Guillermet 1986	Table XI, p. 12, row 2 report
Phase composition	1673	γ + μ + W + fcc fcc: Fe 0.648647, Ni 0.294191, W 0.057162; μ: Fe 0.286316, Ni 0.693305, W 0.020379	experimental	[1] Guillermet 1986 cites Hofmann 1983	Table XI, p. 12, row 1 report
Phase composition	1753	γ + μ + fcc fcc: Fe 0.67205, Ni 0.264594, W 0.063356; μ: Fe 0.313415, Ni 0.664513, W 0.022072	experimental	[1] Guillermet 1986 cites Hofmann 1983	Table XI, p. 12, row 3 report
Phase composition	1753	γ + μ + fcc fcc: Fe 0.636781, Ni 0.270006, W 0.093213; μ: Fe 0.525642, Ni 0.101089, W 0.37327	experimental	[1] Guillermet 1986	Table XI, p. 12, row 4 report

Sources

Reporting papers the values were read from (a value cited from another work names that work in its row).

A. Fernández Guillermet, L. Östlund, Experimental and theoretical study of the phase equilibria in the fe-ni-w system, Metall Trans A 17, 1809-1823 (1986). doi:10.1007/bf02817278

Please cite

R. Arróyave, J. Saal, D. Shin, ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature (version 2026.10; Version 1, machine-extracted), Zenodo (2026). doi:10.5281/zenodo.23735569
R. Arróyave, J. Saal, D. Shin, ORCHID data: umbrella record of the ORCHID datasets (version 2026.10; Version 1, machine-extracted), Zenodo (2026). doi:10.5281/zenodo.23736065

Also cite the original source of every value you use (paper_citation / paper_doi, and cited_dois for values the paper cites from earlier work); B. Hallstedt, The SGTE collection of binary datasets, Calphad 89 (2025) 102833, https://doi.org/10.1016/j.calphad.2025.102833 (CC BY 4.0), and the original assessment named in each file; A. Jain et al., The Materials Project: A materials genome approach to accelerating materials innovation, APL Materials 1 (2013) 011002, https://doi.org/10.1063/1.4812323 (CC BY 4.0); J. E. Saal et al., JOM 65 (2013) 1501, https://doi.org/10.1007/s11837-013-0755-4 and S. Kirklin et al., npj Comput. Mater. 1 (2015) 15010, https://doi.org/10.1038/npjcompumats.2015.10 (CC BY 4.0). Version 1, machine-extracted: values were read by language-model readers constrained to quote their source and checked automatically, and the release was then audited on the printed pages by adversarial audits, an independent second review of fit-facing records and a preliminary human review of a frozen sample. Flags such as accepted and ESPEI-ready record screening results, not certification; known issues are listed in the release notes.

@misc{orchid_literature_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23735569},
  url       = {https://doi.org/10.5281/zenodo.23735569},
  note      = {Version 1, machine-extracted}
}

@misc{orchid_data_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID data: umbrella record of the ORCHID datasets}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23736065},
  url       = {https://doi.org/10.5281/zenodo.23736065},
  note      = {Version 1, machine-extracted}
}