# Li–Sb system

> Li–Sb system: 401 accepted literature values (mixing / partial 351, invariant reaction 23, formation 19, phase equilibrium 6) and 2 calculated phase diagram(s) from ORCHID, each value with evidence class, source, page and quote.

HTML: https://data.orchid-project.org/systems/LI-SB.html · Markdown: https://data.orchid-project.org/systems/LI-SB.md

401 accepted literature values from 2 paper(s) (experimental 387, model 14); 2 calculated phase diagram(s). 11 further extracted value(s) not accepted by the reader-agreement checks are only in the JSON/CSV.

Data: [JSON](https://data.orchid-project.org/literature/systems/LI-SB.json) · [CSV](https://data.orchid-project.org/systems/LI-SB.csv) · [interactive explorer](https://orchid-project.org/data-explorer/#LI-SB) · [interactive phase diagram](https://orchid-project.org/phase-diagrams/#LI-SB/LiSb-17Li.json) · [phases (8)](https://data.orchid-project.org/phases/pages/LI-SB.html) · [papers (bibliography)](https://data.orchid-project.org/bibliography/pages/systems/LI-SB.html) · [Markdown](https://data.orchid-project.org/systems/LI-SB.md)

Table: Accepted values by evidence class

| Evidence class | Values |
|---|---:|
| experimental | 387 |
| model | 14 |

Table: Accepted values by property group

| Property group | Values |
|---|---:|
| invariant reaction | 23 |
| phase transition | 2 |
| phase equilibrium | 6 |
| formation | 19 |
| mixing / partial | 351 |

## Calculated phase diagrams

Binary phase diagrams calculated with pycalphad 0.11.2 from the SGTE binary collection (Hallstedt 2025, CC BY 4.0). Evidence class: model.

Table: Assessments with a calculated phase diagram

| TDB file | Assessment | SHA-256 | Links |
|---|---|---|---|
| LiSb-17Li.tdb | D. Li, A. Beutl, H. Flandorfer, D.M. Cupid, J. Alloys Compd., 701, 186-99(2017). [doi:10.1016/j.jallcom.2016.12.399](https://doi.org/10.1016/j.jallcom.2016.12.399) | `3680314cebef8591dcfe6b87918a1301a48a7cfb5079255751a6c875ba5f6696` | [viewer](https://orchid-project.org/phase-diagrams/#LI-SB/LiSb-17Li.json) · [TDB](https://orchid-project.org/data/databases/sgte-binary/LiSb-17Li.tdb) · [JSON](https://data.orchid-project.org/phase-diagrams/sgte/LiSb-17Li.json) |
| LiSb-17Zha.tdb | F. Zhang, S. Liu, J. Wang, Y. Du, L. Sun, Calphad, 57, 28-36(2017). [doi:10.1016/j.calphad.2017.01.005](https://doi.org/10.1016/j.calphad.2017.01.005) | `69f98315030807278c40e208cd5c226a711d1a40ba15ed41148c0418beea42e2` | [viewer](https://orchid-project.org/phase-diagrams/#LI-SB/LiSb-17Zha.json) · [TDB](https://orchid-project.org/data/databases/sgte-binary/LiSb-17Zha.tdb) · [JSON](https://data.orchid-project.org/phase-diagrams/sgte/LiSb-17Zha.json) |

Table: Calculated three-phase invariants (model, mole fraction of the second component)

| TDB file | T (K) | Phases at the invariant |
|---|---:|---|
| LiSb-17Li.tdb | 864.15 | LI3SB_D018 (x(Sb) 0.25) + LI2SB (x(Sb) 0.33333) + LIQUID (x(Sb) 0.46875) |
| LiSb-17Li.tdb | 743.69 | LI2SB (x(Sb) 0.33333) + LIQUID (x(Sb) 0.58396) + RHOMBOHEDRAL_A7 (x(Sb) 1) |
| LiSb-17Li.tdb | 453.6 | BCC_A2 (x(Sb) 0) + LIQUID (x(Sb) 0) + LI3SB_D018 (x(Sb) 0.25) |
| LiSb-17Zha.tdb | 1160.49 | LIQUID (x(Sb) 0.212) + LI3SB_D03 (x(Sb) 0.25) + LI3SB_D018 (x(Sb) 0.25) |
| LiSb-17Zha.tdb | 1160.49 | LI3SB_D03 (x(Sb) 0.25) + LI3SB_D018 (x(Sb) 0.25) + LIQUID (x(Sb) 0.34174) |
| LiSb-17Zha.tdb | 856.56 | LI3SB_D03 (x(Sb) 0.25) + LI2SB (x(Sb) 0.33333) + LIQUID (x(Sb) 0.45461) |
| LiSb-17Zha.tdb | 739.43 | LI2SB (x(Sb) 0.33333) + LIQUID (x(Sb) 0.5948) + RHOMBOHEDRAL_A7 (x(Sb) 1) |
| LiSb-17Zha.tdb | 441.35 | BCC_A2 (x(Sb) 0) + LIQUID (x(Sb) 0.02066) + LI3SB_D03 (x(Sb) 0.25) |

Convex hulls: [Materials Project DFT hull](https://data.orchid-project.org/hulls/dft-mp/LI/LI-SB.json) · [OQMD DFT hull](https://data.orchid-project.org/hulls/dft-oqmd/LI/LI-SB.json) · [CALPHAD hull LiSb-17Zha](https://data.orchid-project.org/hulls/calphad-sgte/LI/LI-SB--LiSb-17Zha.json)

## Invariant reactions (literature)

Table: Invariant reactions reported in the literature for the Li–Sb system (23)

| T (K) | Reaction / phases | Compositions (mole fraction) | Class | Source | Location | Quote |
|---:|---|---|---|---|---|---|
| 1580.29 | congruent melting: L -> Li3Sb | L: Sb 0.25; Li3Sb: Sb 0.25 | model | [1] Li 2017 | Table 10, p. 11, row 2; `ORC-5W7BRISPIW` |  |
| 1580 | congruent melting: L -> Li3Sb | L: Sb 0.25; Li3Sb: Sb 0.25 | experimental | [1] Li 2017 | Table 10, p. 11, row 1; `ORC-UC2NY4N3J3` |  |
| 1457.15 | congruent melting: Liquid→βLi3Sb | Liquid: Li 0.75; βLi3Sb: Li 0.75, Sb 0.25 | model | [2] Zhang 2017 | Table 4, p. 35, row 11; `ORC-MI5POA3Q3C` |  |
| 1423.15 | congruent melting: Liquid→βLi3Sb | Liquid: Li 0.75, Sb 0.25; βLi3Sb: Li 0.75, Sb 0.25 | experimental | [2] Zhang 2017; _cites ref. 9_ | Table 4, p. 35, row 9; `ORC-4N7TCZKF2R` |  |
| 1223.15 | congruent melting: Liquid→βLi3Sb | Liquid: Li 0.75, Sb 0.25; βLi3Sb: Li 0.75, Sb 0.25 | experimental | [2] Zhang 2017; _cites ref. 11_ | Table 4, p. 35, row 10; `ORC-OGPXRXHX7J` |  |
| 1160.15 | polymorphic: βLi3Sb→αLi3Sb | βLi3Sb: Li 0.75, Sb 0.25; αLi3Sb: Li 0.75, Sb 0.25 | model | [2] Zhang 2017 | Table 4, p. 35, row 8; `ORC-E5LHGLZ5XW` |  |
| 923.15 | polymorphic: βLi3Sb→αLi3Sb | βLi3Sb: Li 0.75, Sb 0.25; αLi3Sb: Li 0.75, Sb 0.25 | experimental | [2] Zhang 2017; _cites ref. 9_ | Table 4, p. 35, row 7; `ORC-VWV2FNM66K` |  |
| 864.15 | L + Li3Sb -> Li2Sb | L: Sb 0.469; Li3Sb: Sb 0.25; Li2Sb: Sb 0.333 | model | [1] Li 2017 | Table 10, p. 11, row 5; `ORC-M2GJRF47QN` |  |
| 863 | L + Li3Sb -> Li2Sb | Li3Sb: Li 0.75, Sb 0.25; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [1] Li 2017 | Table 10, p. 11, row 4; `ORC-VUPN2CMAM5` |  |
| 857.15 | peritectic: Liquid+αLi3Sb→Li2Sb | αLi3Sb: Li 0.75, Sb 0.25; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [2] Zhang 2017; _cites ref. 8_ | Table 4, p. 35, row 5; `ORC-OZ2NU3N4Z2` |  |
| 857 | L + Li3Sb -> Li2Sb | Li3Sb: Li 0.75, Sb 0.25; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [1] Li 2017; _cites Kane 2015_ | Table 10, p. 11, row 3; `ORC-3IEU5VLSTP` |  |
| 856.15 | peritectic: Liquid+αLi3Sb→Li2Sb | Liquid: Li 0.545; αLi3Sb: Li 0.75, Sb 0.25; Li2Sb: Li 0.666667, Sb 0.333333 | model | [2] Zhang 2017 | Table 4, p. 35, row 6; `ORC-P757GBBJR2` |  |
| 744 | eutectic: L -> Li2Sb + (Sb) | L: Sb 0.6; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [1] Li 2017 | Table 10, p. 11, row 7; `ORC-7LU4N27EHR` |  |
| 743.69 | eutectic: L -> Li2Sb + (Sb) | L: Sb 0.584; Li2Sb: Sb 0.333; (Sb): Sb 1 | model | [1] Li 2017 | Table 10, p. 11, row 8; `ORC-7MQPAHGHHI` |  |
| 739.15 | eutectic: Liquid→(Sb)+Li2Sb | Liquid: Li 0.15; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [2] Zhang 2017; _cites ref. 7_ | Table 4, p. 35, row 2; `ORC-25MZWSPD2B` |  |
| 739.15 | eutectic: Liquid→(Sb)+Li2Sb | Liquid: Li 0.405; Li2Sb: Li 0.666667, Sb 0.333333 | model | [2] Zhang 2017 | Table 4, p. 35, row 4; `ORC-2UXGD2GF5I` |  |
| 739.15 | eutectic: Liquid→(Sb)+Li2Sb | Liquid: Li 0.4; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [2] Zhang 2017 | Table 4, p. 35, row 3; `ORC-N2DYGGETMC` |  |
| 733.15 | eutectic: Liquid→(Sb)+Li2Sb | Liquid: Li 0.4; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [2] Zhang 2017; _cites ref. 8_ | Table 4, p. 35, row 1; `ORC-7YXJBAX4BX` |  |
| 733 | eutectic: L -> Li2Sb + (Sb) | L: Sb 0.6; Li2Sb: Li 0.666667, Sb 0.333333 | experimental | [1] Li 2017; _cites Kane 2015_ | Table 10, p. 11, row 6; `ORC-4IZBNNWNE7` |  |
| 453.6 | eutectic: L -> (Li) + Li3Sb | L: Sb 0; (Li): Sb 0; Li3Sb: Sb 0.25 | model | [1] Li 2017 | Table 10, p. 11, row 10; `ORC-DBZFIHV6QH` |  |
| 451 | eutectic: L -> (Li) + Li3Sb | Li3Sb: Li 0.75, Sb 0.25 | experimental | [1] Li 2017 | Table 10, p. 11, row 9; `ORC-6TOBMOYX6B` |  |
| 449.15 | eutectic: Liquid→(Li)+ αLi3Sb | αLi3Sb: Li 0.75, Sb 0.25 | experimental | [2] Zhang 2017; _cites ref. 7_ | Table 4, p. 35, row 12; `ORC-PBDMATUKWI` |  |
| 441.15 | eutectic: Liquid→(Li)+ αLi3Sb | Liquid: Li 0.979; αLi3Sb: Li 0.75, Sb 0.25 | model | [2] Zhang 2017 | Table 4, p. 35, row 13; `ORC-K34GJ2SQJA` |  |

## Formation enthalpies

Literature values in kJ/mol-atom where the per-atom basis is known. DFT columns: the lowest-energy entry at the same composition (Materials Project 2026.04.13, OQMD v1.8; different energy references, never averaged), from [dft_parity.json](https://data.orchid-project.org/literature/dft_parity.json).

Table: Enthalpies of formation, Li–Sb system (9)

| Phase | Compound | Value | T (K) | Class | MP DFT (kJ/mol-atom) | OQMD DFT (kJ/mol-atom) | Source | Location | Quote |
|---|---|---:|---:|---|---:|---:|---|---|---|
| Li2Sb | [Li2Sb](https://data.orchid-project.org/compounds/Li2Sb.html) | -67.8667 kJ/mol-atom | 700.65 | model | -61.478 (mp-aaadjyvo) | -56.263 (oqmd-16940) | [2] Zhang 2017 | Table 5, p. 36, row 3; `ORC-IWVZOUUPGY.46a485` |  |
| Li2Sb | [Li2Sb](https://data.orchid-project.org/compounds/Li2Sb.html) | -66.7 kJ/mol-atom ± 0.5 | 820 | experimental | -61.478 (mp-aaadjyvo) | -56.263 (oqmd-16940) | [1] Li 2017; _cites Terlicka 2016_ [doi](https://doi.org/10.1016/j.jallcom.2016.02.235) | Table 1, p. 3, row 3; `ORC-K6WZU2MCRE` |  |
| Li2Sb | [Li2Sb](https://data.orchid-project.org/compounds/Li2Sb.html) | -65.7667 kJ/mol-atom | 700.65 | experimental | -61.478 (mp-aaadjyvo) | -56.263 (oqmd-16940) | [2] Zhang 2017; _cites ref. 10_ | Table 5, p. 36, row 1; `ORC-QV5TLNQUTY.a8e519` |  |
| Li2Sb | [Li2Sb](https://data.orchid-project.org/compounds/Li2Sb.html) | -65 kJ/mol-atom | 686.65 | experimental | -61.478 (mp-aaadjyvo) | -56.263 (oqmd-16940) | [2] Zhang 2017; _cites ref. 14_ | Table 5, p. 36, row 2; `ORC-WZ43ROHBNB.4b5e87` |  |
| Li3Sb | [Li3Sb](https://data.orchid-project.org/compounds/Li3Sb.html) | -81.5 kJ/mol-atom | 298.15 | experimental | -65.598 (mp-aaaaadbu) | -61.983 (oqmd-646185) | [1] Li 2017; _cites Shchukarev 1954_ | Table 1, p. 3, row 1; `ORC-AVHRPD6MDN` |  |
| Li3Sb | [Li3Sb](https://data.orchid-project.org/compounds/Li3Sb.html) | -76.825 kJ/mol-atom | 700.65 | model | -65.598 (mp-aaaaadbu) | -61.983 (oqmd-646185) | [2] Zhang 2017 | Table 5, p. 36, row 6; `ORC-5XMN7JRI3A.109d66` |  |
| Li3Sb | [Li3Sb](https://data.orchid-project.org/compounds/Li3Sb.html) | -75.25 kJ/mol-atom | 686.65 | experimental | -65.598 (mp-aaaaadbu) | -61.983 (oqmd-646185) | [2] Zhang 2017; _cites ref. 14_ | Table 5, p. 36, row 5; `ORC-4KBCL5U4BH.342b48` |  |
| Li3Sb | [Li3Sb](https://data.orchid-project.org/compounds/Li3Sb.html) | -73.325 kJ/mol-atom | 700.65 | experimental | -65.598 (mp-aaaaadbu) | -61.983 (oqmd-646185) | [2] Zhang 2017; _cites ref. 10_ | Table 5, p. 36, row 4; `ORC-L3ZY532BLT.85a76f` |  |
| Li3Sb | [Li3Sb](https://data.orchid-project.org/compounds/Li3Sb.html) | -70.03 kJ/mol-atom ± 0.3 | 942 | experimental | -65.598 (mp-aaaaadbu) | -61.983 (oqmd-646185) | [1] Li 2017; _cites Terlicka 2016_ [doi](https://doi.org/10.1016/j.jallcom.2016.02.235) | Table 1, p. 3, row 2; `ORC-NNHSFNGPVO` |  |

## Other properties

### Phase transition (2)

Table: Phase transition, Li–Sb system

| Property | Value | T (K) | Phases / composition | Class | Source | Location | Quote |
|---|---:|---:|---|---|---|---|---|
| Phase transition | 1457.15 K | 1457.15 | βLi3Sb | model | [2] Zhang 2017 | p. 9; `ORC-5SUDM4JQBZ.b514c9` | “The calculated melting temperature of βLi3Sb, transition temperature of αLi3Sb→βLi3Sb and eutectic temperature of L→(Li)+αLi3Sb are 1184 oC, 887 oC and 168 oC, which are consistent with the reported data \[7-9, 11\].” |
| Phase transition | 1580 K | 1580 | congruent transformation | experimental | [1] Li 2017 | p. 6; `ORC-3VK4LHEHRJ` | “In the experimental phase diagram of the Li-Sb system, the Li3 Sb compound shows a congruent melting point at 1580 K with a very” |

### Phase equilibrium (6)

Table: Phase equilibrium, Li–Sb system

| Property | Value | T (K) | Phases / composition | Class | Source | Location | Quote |
|---|---:|---:|---|---|---|---|---|
| Phase assemblage |  |  | (Sb) + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.15, Sb 0.85_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 1; `ORC-BNUHHV3U2K` |  |
| Phase assemblage |  |  | (Sb) + Li2Sb + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.45, Sb 0.55_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 4; `ORC-DSXJA6EVH4` |  |
| Phase assemblage |  |  | (Sb) + Li2Sb + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.5, Sb 0.5_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 5; `ORC-JWLPQPPKTR` |  |
| Phase assemblage |  |  | (Sb) + Li2Sb + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.25, Sb 0.75_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 2; `ORC-U5MK6AB6FI` |  |
| Phase assemblage |  |  | (Sb) + Li2Sb + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.4, Sb 0.6_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 3; `ORC-Z5POMSNZIQ` |  |
| Phase assemblage |  |  | (Sb) + Li2Sb + αLi3Sb + Li3Sb + Eutectic (Sb)+ Li2Sb; _alloy: Li 0.4, Sb 0.6_ | experimental | [2] Zhang 2017 | Table 1, p. 32, row 6; `ORC-RICJPVQS3V` |  |

### Formation (10)

Table: Formation, Li–Sb system

| Property | Value | T (K) | Phases / composition | Class | Source | Location | Quote |
|---|---:|---:|---|---|---|---|---|
| Entropy of formation; _printed: ΔSf_ | -9 J/mol-atom/K | 686.65 | Li2Sb; _alloy: Sb 0.333333_ | experimental | [2] Zhang 2017; _cites ref. 14_ | Table 5, p. 36, row 2; `ORC-WZ43ROHBNB.01b270` |  |
| Entropy of formation; _printed: ΔSf_ | -15 J/mol-atom/K | 686.65 | Li3Sb; _alloy: Sb 0.25_ | experimental | [2] Zhang 2017; _cites ref. 14_ | Table 5, p. 36, row 5; `ORC-4KBCL5U4BH.046030` |  |
| Entropy of formation; _printed: ΔSf_ | -13.0667 J/mol-atom/K | 700.65 | Li2Sb; _alloy: Sb 0.333333_ | model | [2] Zhang 2017 | Table 5, p. 36, row 3; `ORC-IWVZOUUPGY.04708b` |  |
| Entropy of formation; _printed: ΔSf_ | -10.6333 J/mol-atom/K | 700.65 | Li2Sb; _alloy: Sb 0.333333_ | experimental | [2] Zhang 2017; _cites ref. 10_ | Table 5, p. 36, row 1; `ORC-QV5TLNQUTY.1f29c7` |  |
| Entropy of formation; _printed: ΔSf_ | -16.4375 J/mol-atom/K | 700.65 | Li3Sb; _alloy: Sb 0.25_ | model | [2] Zhang 2017 | Table 5, p. 36, row 6; `ORC-5XMN7JRI3A.15497c` |  |
| Entropy of formation; _printed: ΔSf_ | -12.3 J/mol-atom/K | 700.65 | Li3Sb; _alloy: Sb 0.25_ | experimental | [2] Zhang 2017; _cites ref. 10_ | Table 5, p. 36, row 4; `ORC-L3ZY532BLT.f04169` |  |
| Gibbs energy of formation; _printed: ΔfGLi2Sb_ | 58.9 kJ/mol-atom | 630 | Li2Sb; _alloy: Sb 0.333333_ | experimental | [1] Li 2017; _cites Nikitin 1982_ | Table 1, p. 3, row 4; `ORC-FWLVF5XETV` |  |
| Gibbs energy of formation; _printed: ΔfGLi3Sb_ | 65.4 kJ/mol-atom | 630 | Li3Sb; _alloy: Sb 0.25_ | experimental | [1] Li 2017; _cites Nikitin 1982_ | Table 1, p. 3, row 6; `ORC-BDUZKOBQSG` |  |
| Gibbs energy of formation; _printed: ΔfGLi2Sb_ | 58.2 kJ/mol-atom | 723 | Li2Sb; _alloy: Sb 0.333333_ | experimental | [1] Li 2017; _cites Nikitin 1982_ | Table 1, p. 3, row 5; `ORC-SGNKL2MPDJ` |  |
| Gibbs energy of formation; _printed: ΔfGLi3Sb_ | 64.3 kJ/mol-atom | 723 | Li3Sb; _alloy: Sb 0.25_ | experimental | [1] Li 2017; _cites Nikitin 1982_ | Table 1, p. 3, row 7; `ORC-3VTJ5UM27P` |  |

### Mixing / partial (351)

Table: Mixing / partial, Li–Sb system

| Property | Value | T (K) | Phases / composition | Class | Source | Location | Quote |
|---|---:|---:|---|---|---|---|---|
| Enthalpy of mixing; _printed: ΔmixH_ | -54.709 kJ/mol (basis unstated) ± 1.504 | 929 | liquid; _alloy: Li 0.55589, Sb 0.44411_ | experimental | [1] Li 2017 | Table 4, p. 7, row 20; `ORC-2CKRUYB3DW.6cdbc4` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -36.467 kJ/mol (basis unstated) ± 0.951 | 929 | liquid; _alloy: Li 0.39594, Sb 0.60406_ | experimental | [1] Li 2017 | Table 4, p. 7, row 12; `ORC-2XDURIRRQO.365a2d` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -38.922 kJ/mol (basis unstated) ± 1.018 | 929 | liquid; _alloy: Li 0.4195, Sb 0.5805_ | experimental | [1] Li 2017 | Table 4, p. 7, row 13; `ORC-3FN4FC4ZLX.bf69c4` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -57.425 kJ/mol (basis unstated) ± 1.573 | 929 | liquid; _alloy: Li 0.57397, Sb 0.42603_ | experimental | [1] Li 2017 | Table 4, p. 7, row 21; `ORC-3IRQ6IJTIA.6becea` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -19.303 kJ/mol (basis unstated) ± 0.457 | 929 | liquid; _alloy: Li 0.22893, Sb 0.77107_ | experimental | [1] Li 2017 | Table 4, p. 7, row 6; `ORC-5BPQVDHI4K.19a0a2` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -67.44 kJ/mol (basis unstated) ± 1.898 | 929 | liquid; _alloy: Li 0.63699, Sb 0.36301_ | experimental | [1] Li 2017 | Table 4, p. 7, row 25; `ORC-5MMGHF6J5J.6f26fc` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -65.104 kJ/mol (basis unstated) ± 1.735 | 929 | liquid; _alloy: Li 0.62243, Sb 0.37757_ | experimental | [1] Li 2017 | Table 4, p. 7, row 24; `ORC-7CK67MT5ZO.32b5fd` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -59.991 kJ/mol (basis unstated) ± 1.644 | 929 | liquid; _alloy: Li 0.59085, Sb 0.40915_ | experimental | [1] Li 2017 | Table 4, p. 7, row 22; `ORC-AEQLRV4BGJ.8f8128` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -28.439 kJ/mol (basis unstated) ± 0.686 | 929 | liquid; _alloy: Li 0.31949, Sb 0.68051_ | experimental | [1] Li 2017 | Table 4, p. 7, row 9; `ORC-C67CG5YGGA.18cb8e` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -52.657 kJ/mol (basis unstated) ± 1.434 | 929 | liquid; _alloy: Li 0.53919, Sb 0.46081_ | experimental | [1] Li 2017 | Table 4, p. 7, row 19; `ORC-GGZEKQU7S4.1ddce8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -41.514 kJ/mol (basis unstated) ± 1.138 | 929 | liquid; _alloy: Li 0.44217, Sb 0.55783_ | experimental | [1] Li 2017 | Table 4, p. 7, row 14; `ORC-GV6USGVCSH.8663fc` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -10.827 kJ/mol (basis unstated) ± 0.262 | 929 | liquid; _alloy: Li 0.12088, Sb 0.87912_ | experimental | [1] Li 2017 | Table 4, p. 7, row 3; `ORC-HNMU5NSLAR.3a9200` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -50.605 kJ/mol (basis unstated) ± 1.36 | 929 | liquid; _alloy: Li 0.52217, Sb 0.47783_ | experimental | [1] Li 2017 | Table 4, p. 7, row 18; `ORC-IQH7SQMS7C.2e314b` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -48.38 kJ/mol (basis unstated) ± 1.306 | 929 | liquid; _alloy: Li 0.50387, Sb 0.49613_ | experimental | [1] Li 2017 | Table 4, p. 7, row 17; `ORC-KV65HOC7S2.575b6c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -62.538 kJ/mol (basis unstated) ± 1.709 | 929 | liquid; _alloy: Li 0.60678, Sb 0.39322_ | experimental | [1] Li 2017 | Table 4, p. 7, row 23; `ORC-LNA2VB3CTL.6ec5e3` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -17.384 kJ/mol (basis unstated) ± 0.419 | 929 | liquid; _alloy: Li 0.195, Sb 0.805_ | experimental | [1] Li 2017 | Table 4, p. 7, row 5; `ORC-N6ZLIFXSFF.99d6ec` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -7.456 kJ/mol (basis unstated) ± 0.18 | 929 | liquid; _alloy: Li 0.08298, Sb 0.91702_ | experimental | [1] Li 2017 | Table 4, p. 7, row 2; `ORC-NGIDTXSSGC.70deab` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -31.22 kJ/mol (basis unstated) ± 0.756 | 929 | liquid; _alloy: Li 0.3465, Sb 0.6535_ | experimental | [1] Li 2017 | Table 4, p. 7, row 10; `ORC-NYQWQ3YHDC.af8166` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -22.065 kJ/mol (basis unstated) ± 0.523 | 929 | liquid; _alloy: Li 0.26107, Sb 0.73893_ | experimental | [1] Li 2017 | Table 4, p. 7, row 7; `ORC-ORCXUYWCRT.43b3a3` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -33.938 kJ/mol (basis unstated) ± 0.825 | 929 | liquid; _alloy: Li 0.37191, Sb 0.62809_ | experimental | [1] Li 2017 | Table 4, p. 7, row 11; `ORC-QX6HDKLOPI.3b44f8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -25.444 kJ/mol (basis unstated) ± 0.61 | 929 | liquid; _alloy: Li 0.29139, Sb 0.70861_ | experimental | [1] Li 2017 | Table 4, p. 7, row 8; `ORC-RK3S6OHT26.7ca9c9` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -43.954 kJ/mol (basis unstated) ± 1.194 | 929 | liquid; _alloy: Li 0.46417, Sb 0.53583_ | experimental | [1] Li 2017 | Table 4, p. 7, row 15; `ORC-SIGVDMMRFD.2d0f64` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -46.212 kJ/mol (basis unstated) ± 1.252 | 929 | liquid; _alloy: Li 0.48458, Sb 0.51542_ | experimental | [1] Li 2017 | Table 4, p. 7, row 16; `ORC-VLOVDRLDXP.222dfd` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -14.183 kJ/mol (basis unstated) ± 0.343 | 929 | liquid; _alloy: Li 0.15795, Sb 0.84205_ | experimental | [1] Li 2017 | Table 4, p. 7, row 4; `ORC-W6ZAYH4AC4.04a014` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -3.788 kJ/mol (basis unstated) ± 0.092 | 929 | liquid; _alloy: Li 0.04221, Sb 0.95779_ | experimental | [1] Li 2017 | Table 4, p. 7, row 1; `ORC-YXN56HZPNM.5dbe46` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -5.676 kJ/mol (basis unstated) ± 0.067 | 979 | UNKNOWN; _alloy: Li 0.06354, Sb 0.93646_ | experimental | [1] Li 2017 | Table 5, p. 7, row 2; `ORC-27ENRZHFIH.bb8a88` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -12.56 kJ/mol (basis unstated) ± 0.142 | 979 | UNKNOWN; _alloy: Li 0.13581, Sb 0.86419_ | experimental | [1] Li 2017 | Table 5, p. 7, row 4; `ORC-2QGHJJNDFX.677f28` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -50.993 kJ/mol (basis unstated) ± 0.152 | 979 | UNKNOWN; _alloy: Li 0.51975, Sb 0.48025_ | experimental | [1] Li 2017 | Table 7, p. 9, row 23; `ORC-2XJVL52ZZS.8a49ec` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -56.478 kJ/mol (basis unstated) ± 0.131 | 979 | UNKNOWN; _alloy: Li 0.56853, Sb 0.43147_ | experimental | [1] Li 2017 | Table 7, p. 9, row 18; `ORC-324KCUAJTB.3c7513` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -54.74 kJ/mol (basis unstated) ± 0.672 | 979 | UNKNOWN; _alloy: Li 0.55405, Sb 0.44595_ | experimental | [1] Li 2017 | Table 5, p. 7, row 20; `ORC-3BWGXP6SDT.52e3e9` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -76.713 kJ/mol (basis unstated) ± 0.034 | 979 | UNKNOWN; _alloy: Li 0.70319, Sb 0.29681_ | experimental | [1] Li 2017 | Table 7, p. 9, row 6; `ORC-3UMK4HZRHK.4928c5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -33.756 kJ/mol (basis unstated) ± 0.409 | 979 | UNKNOWN; _alloy: Li 0.3607, Sb 0.6393_ | experimental | [1] Li 2017 | Table 5, p. 7, row 11; `ORC-3YALOHDNR3.0de3fc` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -78.247 kJ/mol (basis unstated) ± 0.026 | 979 | UNKNOWN; _alloy: Li 0.71316, Sb 0.28684_ | experimental | [1] Li 2017 | Table 7, p. 9, row 5; `ORC-5BEUS7NSSP.657f69` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -50.82 kJ/mol (basis unstated) ± 0.622 | 979 | UNKNOWN; _alloy: Li 0.5196, Sb 0.4804_ | experimental | [1] Li 2017 | Table 5, p. 7, row 18; `ORC-5EULFO2SNI.7ff09c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -8.631 kJ/mol (basis unstated) ± 0.102 | 979 | UNKNOWN; _alloy: Li 0.09782, Sb 0.90218_ | experimental | [1] Li 2017 | Table 5, p. 7, row 3; `ORC-7CQZM6YFNQ.9b6728` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -15.987 kJ/mol (basis unstated) ± 0.183 | 979 | UNKNOWN; _alloy: Li 0.17183, Sb 0.82817_ | experimental | [1] Li 2017 | Table 5, p. 7, row 5; `ORC-7IZSXRGLA5.1e62f8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -59.616 kJ/mol (basis unstated) ± 0.116 | 979 | UNKNOWN; _alloy: Li 0.58969, Sb 0.41031_ | experimental | [1] Li 2017 | Table 7, p. 9, row 16; `ORC-A23FUSO6HP.701cb7` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -81.166 kJ/mol (basis unstated) ± 0.012 | 979 | UNKNOWN; _alloy: Li 0.73259, Sb 0.26741_ | experimental | [1] Li 2017 | Table 7, p. 9, row 3; `ORC-AD34SRG5AB.4e4eb1` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -66.666 kJ/mol (basis unstated) ± 0.837 | 979 | UNKNOWN; _alloy: Li 0.6339, Sb 0.3661_ | experimental | [1] Li 2017 | Table 5, p. 7, row 25; `ORC-AGU7ATIYGJ.57d46e` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -25.603 kJ/mol (basis unstated) ± 0.3 | 979 | UNKNOWN; _alloy: Li 0.27444, Sb 0.72556_ | experimental | [1] Li 2017 | Table 5, p. 7, row 8; `ORC-ARISD7LQXQ.8f30cc` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -62.949 kJ/mol (basis unstated) ± 0.1 | 979 | UNKNOWN; _alloy: Li 0.6116, Sb 0.3884_ | experimental | [1] Li 2017 | Table 7, p. 9, row 14; `ORC-AUKWBMGA5C.ddb196` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -36.421 kJ/mol (basis unstated) ± 0.442 | 979 | UNKNOWN; _alloy: Li 0.38682, Sb 0.61318_ | experimental | [1] Li 2017 | Table 5, p. 7, row 12; `ORC-C64TM3NLHR.d751c9` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -56.556 kJ/mol (basis unstated) ± 0.695 | 979 | UNKNOWN; _alloy: Li 0.56975, Sb 0.43025_ | experimental | [1] Li 2017 | Table 5, p. 7, row 21; `ORC-CJLV4LOPNF.f82c71` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -52.005 kJ/mol (basis unstated) ± 0.148 | 979 | UNKNOWN; _alloy: Li 0.52902, Sb 0.47098_ | experimental | [1] Li 2017 | Table 7, p. 9, row 22; `ORC-CXYDLQ5DZE.5e0076` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -2.726 kJ/mol (basis unstated) ± 0.033 | 979 | UNKNOWN; _alloy: Li 0.02989, Sb 0.97011_ | experimental | [1] Li 2017 | Table 5, p. 7, row 1; `ORC-DGXTGV74FJ.6ab7ef` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -61.113 kJ/mol (basis unstated) ± 0.758 | 979 | UNKNOWN; _alloy: Li 0.60082, Sb 0.39918_ | experimental | [1] Li 2017 | Table 5, p. 7, row 23; `ORC-DSM7RNGM22.155939` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -48.64 kJ/mol (basis unstated) ± 0.594 | 979 | UNKNOWN; _alloy: Li 0.50076, Sb 0.49924_ | experimental | [1] Li 2017 | Table 5, p. 7, row 17; `ORC-EGWMVFTMZP.464734` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -30.975 kJ/mol (basis unstated) ± 0.375 | 979 | UNKNOWN; _alloy: Li 0.33276, Sb 0.66724_ | experimental | [1] Li 2017 | Table 5, p. 7, row 10; `ORC-EOL5JCK3PY.e00397` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -75.156 kJ/mol (basis unstated) ± 0.041 | 979 | UNKNOWN; _alloy: Li 0.69267, Sb 0.30733_ | experimental | [1] Li 2017 | Table 7, p. 9, row 7; `ORC-F4A2JMFGJH.47c2b7` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -61.236 kJ/mol (basis unstated) ± 0.109 | 979 | UNKNOWN; _alloy: Li 0.60055, Sb 0.39945_ | experimental | [1] Li 2017 | Table 7, p. 9, row 15; `ORC-FIQ7BNHLFU.2b0752` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -83.702 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.75, Sb 0.25_ | experimental | [1] Li 2017 | Table 7, p. 9, row 1; `ORC-J3XQAQG2DV` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -63.529 kJ/mol (basis unstated) ± 0.793 | 979 | UNKNOWN; _alloy: Li 0.61559, Sb 0.38441_ | experimental | [1] Li 2017 | Table 5, p. 7, row 24; `ORC-JNPKE2TTDJ.4011b2` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -68.022 kJ/mol (basis unstated) ± 0.076 | 979 | UNKNOWN; _alloy: Li 0.64517, Sb 0.35483_ | experimental | [1] Li 2017 | Table 7, p. 9, row 11; `ORC-KLVT4YVNCO.525ff5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -54.2 kJ/mol (basis unstated) ± 0.14 | 979 | UNKNOWN; _alloy: Li 0.54823, Sb 0.45177_ | experimental | [1] Li 2017 | Table 7, p. 9, row 20; `ORC-MMQ6QORTQE.0773c8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -50.019 kJ/mol (basis unstated) ± 0.155 | 979 | UNKNOWN; _alloy: Li 0.51057, Sb 0.48943_ | experimental | [1] Li 2017 | Table 7, p. 9, row 24; `ORC-OGB5BHFJ44.96025e` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -82.463 kJ/mol (basis unstated) ± 0.006 | 979 | UNKNOWN; _alloy: Li 0.74165, Sb 0.25835_ | experimental | [1] Li 2017 | Table 7, p. 9, row 2; `ORC-PCZK7MQCTV.e272ce` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -46.476 kJ/mol (basis unstated) ± 0.567 | 979 | UNKNOWN; _alloy: Li 0.4805, Sb 0.5195_ | experimental | [1] Li 2017 | Table 5, p. 7, row 16; `ORC-PJ7QENEB33.439622` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -19.223 kJ/mol (basis unstated) ± 0.221 | 979 | UNKNOWN; _alloy: Li 0.20836, Sb 0.79164_ | experimental | [1] Li 2017 | Table 5, p. 7, row 6; `ORC-PT3AK5E5VQ.f07da2` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -52.826 kJ/mol (basis unstated) ± 0.647 | 979 | UNKNOWN; _alloy: Li 0.53722, Sb 0.46278_ | experimental | [1] Li 2017 | Table 5, p. 7, row 19; `ORC-REX4O7CVVS.a62422` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -28.591 kJ/mol (basis unstated) ± 0.337 | 979 | UNKNOWN; _alloy: Li 0.30413, Sb 0.69587_ | experimental | [1] Li 2017 | Table 5, p. 7, row 9; `ORC-RJVTZB7JFG.662ace` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -71.504 kJ/mol (basis unstated) ± 0.059 | 979 | UNKNOWN; _alloy: Li 0.66854, Sb 0.33146_ | experimental | [1] Li 2017 | Table 7, p. 9, row 9; `ORC-RLTCUJXUAN.d9082c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -55.291 kJ/mol (basis unstated) ± 0.136 | 979 | UNKNOWN; _alloy: Li 0.5582, Sb 0.4418_ | experimental | [1] Li 2017 | Table 7, p. 9, row 19; `ORC-SCT4AX4CNS.161b8b` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -44.206 kJ/mol (basis unstated) ± 0.539 | 979 | UNKNOWN; _alloy: Li 0.4587, Sb 0.5413_ | experimental | [1] Li 2017 | Table 5, p. 7, row 15; `ORC-TSSLBQG7IF.0941a5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -79.778 kJ/mol (basis unstated) ± 0.019 | 979 | UNKNOWN; _alloy: Li 0.7234, Sb 0.2766_ | experimental | [1] Li 2017 | Table 7, p. 9, row 4; `ORC-U46GIDWBAC.033dbe` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -64.708 kJ/mol (basis unstated) ± 0.091 | 979 | UNKNOWN; _alloy: Li 0.62282, Sb 0.37718_ | experimental | [1] Li 2017 | Table 7, p. 9, row 13; `ORC-U4AXTSYQAU.da0512` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -22.393 kJ/mol (basis unstated) ± 0.26 | 979 | UNKNOWN; _alloy: Li 0.24245, Sb 0.75755_ | experimental | [1] Li 2017 | Table 5, p. 7, row 7; `ORC-U6YCP2D4CE.814b84` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -41.613 kJ/mol (basis unstated) ± 0.507 | 979 | UNKNOWN; _alloy: Li 0.43499, Sb 0.56501_ | experimental | [1] Li 2017 | Table 5, p. 7, row 14; `ORC-U76E3N3IBK.26f8f0` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -39.142 kJ/mol (basis unstated) ± 0.476 | 979 | UNKNOWN; _alloy: Li 0.41167, Sb 0.58833_ | experimental | [1] Li 2017 | Table 5, p. 7, row 13; `ORC-VCFZCCR356.9b7115` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -48.977 kJ/mol (basis unstated) ± 0.159 | 979 | UNKNOWN; _alloy: Li 0.50104, Sb 0.49896_ | experimental | [1] Li 2017 | Table 7, p. 9, row 25; `ORC-VF4OBQG2UZ.338fcb` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -52.991 kJ/mol (basis unstated) ± 0.145 | 979 | UNKNOWN; _alloy: Li 0.53851, Sb 0.46149_ | experimental | [1] Li 2017 | Table 7, p. 9, row 21; `ORC-WLL5KIGXCE.bec4ac` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -69.784 kJ/mol (basis unstated) ± 0.067 | 979 | UNKNOWN; _alloy: Li 0.65666, Sb 0.34334_ | experimental | [1] Li 2017 | Table 7, p. 9, row 10; `ORC-WNJNP47VAM.3fac9e` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -66.382 kJ/mol (basis unstated) ± 0.083 | 979 | UNKNOWN; _alloy: Li 0.63408, Sb 0.36592_ | experimental | [1] Li 2017 | Table 7, p. 9, row 12; `ORC-YF5XFHR4R5.8a2c7a` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -73.288 kJ/mol (basis unstated) ± 0.05 | 979 | UNKNOWN; _alloy: Li 0.68064, Sb 0.31936_ | experimental | [1] Li 2017 | Table 7, p. 9, row 8; `ORC-YFEPYD4OTH.790ebb` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -58.629 kJ/mol (basis unstated) ± 0.722 | 979 | UNKNOWN; _alloy: Li 0.58518, Sb 0.41482_ | experimental | [1] Li 2017 | Table 5, p. 7, row 22; `ORC-YGRYUHWU3K.44ba39` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -58.027 kJ/mol (basis unstated) ± 0.124 | 979 | UNKNOWN; _alloy: Li 0.57897, Sb 0.42103_ | experimental | [1] Li 2017 | Table 7, p. 9, row 17; `ORC-ZGOVESY4GA.9f76f9` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -47.912 kJ/mol (basis unstated) ± 0.163 | 979 | UNKNOWN; _alloy: Li 0.49161, Sb 0.50839_ | experimental | [1] Li 2017 | Table 7, p. 9, row 26; `ORC-ZOINEUQ6R5.fbd9e8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -29.427 kJ/mol (basis unstated) ± 0.34 | 979 | liquid; _alloy: Li 0.90916, Sb 0.09084_ | experimental | [1] Li 2017 | Table 2, p. 5, row 21; `ORC-366KWTOBRX.2a89bd` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -26.461 kJ/mol (basis unstated) ± 0.306 | 979 | liquid; _alloy: Li 0.91809, Sb 0.08191_ | experimental | [1] Li 2017 | Table 2, p. 5, row 19; `ORC-4ZUNGQUW25.0a396d` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -0.939 kJ/mol (basis unstated) ± 0.011 | 979 | liquid; _alloy: Li 0.99647, Sb 0.00353_ | experimental | [1] Li 2017 | Table 2, p. 5, row 1; `ORC-5NZ545FAPJ.027e9e` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -3.071 kJ/mol (basis unstated) ± 0.035 | 979 | liquid; _alloy: Li 0.98906, Sb 0.01094_ | experimental | [1] Li 2017 | Table 2, p. 5, row 3; `ORC-5RTTGBYBLH.96385b` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -13.683 kJ/mol (basis unstated) ± 0.158 | 979 | liquid; _alloy: Li 0.95653, Sb 0.04347_ | experimental | [1] Li 2017 | Table 2, p. 5, row 11; `ORC-BBVSGB56XG.6425a1` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -15.084 kJ/mol (basis unstated) ± 0.174 | 979 | liquid; _alloy: Li 0.9523, Sb 0.0477_ | experimental | [1] Li 2017 | Table 2, p. 5, row 12; `ORC-CK4YSGL7IJ.ffa195` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -12.282 kJ/mol (basis unstated) ± 0.141 | 979 | liquid; _alloy: Li 0.96075, Sb 0.03925_ | experimental | [1] Li 2017 | Table 2, p. 5, row 10; `ORC-DCQYNUYZK5.5adfea` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -9.631 kJ/mol (basis unstated) ± 0.111 | 979 | liquid; _alloy: Li 0.96892, Sb 0.03108_ | experimental | [1] Li 2017 | Table 2, p. 5, row 8; `ORC-ECIHSYUDRC.11d1bb` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -16.487 kJ/mol (basis unstated) ± 0.19 | 979 | liquid; _alloy: Li 0.94806, Sb 0.05194_ | experimental | [1] Li 2017 | Table 2, p. 5, row 13; `ORC-EZXO34WQZ3.09362c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -5.603 kJ/mol (basis unstated) ± 0.064 | 979 | liquid; _alloy: Li 0.98125, Sb 0.01875_ | experimental | [1] Li 2017 | Table 2, p. 5, row 5; `ORC-GGF3AVZN5J.b2016c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -27.934 kJ/mol (basis unstated) ± 0.323 | 979 | liquid; _alloy: Li 0.91368, Sb 0.08632_ | experimental | [1] Li 2017 | Table 2, p. 5, row 20; `ORC-JK5N7SNTIR.d22270` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -17.886 kJ/mol (basis unstated) ± 0.207 | 979 | liquid; _alloy: Li 0.94385, Sb 0.05615_ | experimental | [1] Li 2017 | Table 2, p. 5, row 14; `ORC-L33SX3YAL7.fa70d0` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -10.959 kJ/mol (basis unstated) ± 0.126 | 979 | liquid; _alloy: Li 0.96482, Sb 0.03518_ | experimental | [1] Li 2017 | Table 2, p. 5, row 9; `ORC-ND427AX3LA.56d405` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -34.151 kJ/mol (basis unstated) ± 0.396 | 979 | liquid; _alloy: Li 0.89506, Sb 0.10494_ | experimental | [1] Li 2017 | Table 2, p. 5, row 24; `ORC-QC5K7ODIQI.ac5d9f` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -4.289 kJ/mol (basis unstated) ± 0.049 | 979 | liquid; _alloy: Li 0.9852, Sb 0.0148_ | experimental | [1] Li 2017 | Table 2, p. 5, row 4; `ORC-QMOW2L7IX7.b85803` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -20.764 kJ/mol (basis unstated) ± 0.24 | 979 | liquid; _alloy: Li 0.93524, Sb 0.06476_ | experimental | [1] Li 2017 | Table 2, p. 5, row 16; `ORC-QOCRQBJDUB.6f0e5d` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -30.943 kJ/mol (basis unstated) ± 0.358 | 979 | liquid; _alloy: Li 0.90458, Sb 0.09542_ | experimental | [1] Li 2017 | Table 2, p. 5, row 22; `ORC-QVRKZ3JDES.eaf36f` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -32.559 kJ/mol (basis unstated) ± 0.377 | 979 | liquid; _alloy: Li 0.8998, Sb 0.1002_ | experimental | [1] Li 2017 | Table 2, p. 5, row 23; `ORC-QXNLTOYRPC.e8c437` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -22.169 kJ/mol (basis unstated) ± 0.256 | 979 | liquid; _alloy: Li 0.93095, Sb 0.06905_ | experimental | [1] Li 2017 | Table 2, p. 5, row 17; `ORC-S2UL3AKO7G.92cdb8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -1.96 kJ/mol (basis unstated) ± 0.022 | 979 | liquid; _alloy: Li 0.99287, Sb 0.00713_ | experimental | [1] Li 2017 | Table 2, p. 5, row 2; `ORC-UCAWQ7TJ6P.414e38` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -23.593 kJ/mol (basis unstated) ± 0.271 | 979 | liquid; _alloy: Li 0.92669, Sb 0.07331_ | experimental | [1] Li 2017 | Table 2, p. 5, row 18; `ORC-V3ZLX7NUVW.254cf3` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -6.938 kJ/mol (basis unstated) ± 0.08 | 979 | liquid; _alloy: Li 0.97716, Sb 0.02284_ | experimental | [1] Li 2017 | Table 2, p. 5, row 6; `ORC-VEF6TLJI5M.1c3b5c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -8.29 kJ/mol (basis unstated) ± 0.095 | 979 | liquid; _alloy: Li 0.97303, Sb 0.02697_ | experimental | [1] Li 2017 | Table 2, p. 5, row 7; `ORC-W5YFYFLRKV.f13a3c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -19.318 kJ/mol (basis unstated) ± 0.223 | 979 | liquid; _alloy: Li 0.93955, Sb 0.06045_ | experimental | [1] Li 2017 | Table 2, p. 5, row 15; `ORC-XQBHD62QNB.417385` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -83.702 kJ/mol (basis unstated) | 1080 | UNKNOWN; _alloy: Li 0.75, Sb 0.25_ | experimental | [1] Li 2017 | Table 8, p. 9, row 1; `ORC-O57HKFBW6L.5a177a` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -24.169 kJ/mol (basis unstated) ± 0.334 | 1080 | liquid; _alloy: Li 0.92311, Sb 0.07689_ | experimental | [1] Li 2017 | Table 3, p. 6, row 20; `ORC-2BQHK4P4FL.8f72b0` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -8.734 kJ/mol (basis unstated) ± 0.134 | 1080 | liquid; _alloy: Li 0.96895, Sb 0.03105_ | experimental | [1] Li 2017 | Table 3, p. 6, row 9; `ORC-2C53JADKMD.a61c39` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -2.279 kJ/mol (basis unstated) ± 0.034 | 1080 | liquid; _alloy: Li 0.99046, Sb 0.00954_ | experimental | [1] Li 2017 | Table 3, p. 6, row 3; `ORC-5P37AKXDJA.d0b2b7` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -4.053 kJ/mol (basis unstated) ± 0.061 | 1080 | liquid; _alloy: Li 0.98352, Sb 0.01648_ | experimental | [1] Li 2017 | Table 3, p. 6, row 5; `ORC-5QHCOCHWGW.b7b3bd` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -32.896 kJ/mol (basis unstated) ± 0.474 | 1080 | liquid; _alloy: Li 0.89744, Sb 0.10256_ | experimental | [1] Li 2017 | Table 3, p. 6, row 25; `ORC-5ZU4LEKRXD.1dc1ab` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -18.076 kJ/mol (basis unstated) ± 0.282 | 1080 | liquid; _alloy: Li 0.94118, Sb 0.05882_ | experimental | [1] Li 2017 | Table 3, p. 6, row 16; `ORC-622PGZM3T2.fef96a` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -16.673 kJ/mol (basis unstated) ± 0.26 | 1080 | liquid; _alloy: Li 0.9454, Sb 0.0546_ | experimental | [1] Li 2017 | Table 3, p. 6, row 15; `ORC-63WJIQMRVL.c4bbd1` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -11.352 kJ/mol (basis unstated) ± 0.176 | 1080 | liquid; _alloy: Li 0.9612, Sb 0.0388_ | experimental | [1] Li 2017 | Table 3, p. 6, row 11; `ORC-A7W3KER6E5.1f57dd` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -6.219 kJ/mol (basis unstated) ± 0.094 | 1080 | liquid; _alloy: Li 0.97647, Sb 0.02353_ | experimental | [1] Li 2017 | Table 3, p. 6, row 7; `ORC-AXC7ARC6Y6.d4e3d1` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -5.074 kJ/mol (basis unstated) ± 0.076 | 1080 | liquid; _alloy: Li 0.98001, Sb 0.01999_ | experimental | [1] Li 2017 | Table 3, p. 6, row 6; `ORC-CC4ZATIHZY.672cd2` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -20.784 kJ/mol (basis unstated) ± 0.295 | 1080 | liquid; _alloy: Li 0.93296, Sb 0.06704_ | experimental | [1] Li 2017 | Table 3, p. 6, row 18; `ORC-GV7ELY7DVL.858eec` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -7.443 kJ/mol (basis unstated) ± 0.114 | 1080 | liquid; _alloy: Li 0.9728, Sb 0.0272_ | experimental | [1] Li 2017 | Table 3, p. 6, row 8; `ORC-IT7YSQMHF6.db716d` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -27.627 kJ/mol (basis unstated) ± 0.389 | 1080 | liquid; _alloy: Li 0.91292, Sb 0.08708_ | experimental | [1] Li 2017 | Table 3, p. 6, row 22; `ORC-LS2LFPX7UP.701c62` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -15.255 kJ/mol (basis unstated) ± 0.237 | 1080 | liquid; _alloy: Li 0.94958, Sb 0.05042_ | experimental | [1] Li 2017 | Table 3, p. 6, row 14; `ORC-LTGY7ET35B.70862c` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -1.483 kJ/mol (basis unstated) ± 0.022 | 1080 | liquid; _alloy: Li 0.99376, Sb 0.00624_ | experimental | [1] Li 2017 | Table 3, p. 6, row 2; `ORC-N4R4VXHYYS.63bbe6` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -12.656 kJ/mol (basis unstated) ± 0.196 | 1080 | liquid; _alloy: Li 0.95731, Sb 0.04269_ | experimental | [1] Li 2017 | Table 3, p. 6, row 12; `ORC-OWJSHDZEA6.2ee18d` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -13.96 kJ/mol (basis unstated) ± 0.217 | 1080 | liquid; _alloy: Li 0.95344, Sb 0.04656_ | experimental | [1] Li 2017 | Table 3, p. 6, row 13; `ORC-P5GGFOWMDH.1f2213` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -31.098 kJ/mol (basis unstated) ± 0.445 | 1080 | liquid; _alloy: Li 0.90271, Sb 0.09729_ | experimental | [1] Li 2017 | Table 3, p. 6, row 24; `ORC-PRVEMNGLQK.9f59f5` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -10.023 kJ/mol (basis unstated) ± 0.155 | 1080 | liquid; _alloy: Li 0.96508, Sb 0.03492_ | experimental | [1] Li 2017 | Table 3, p. 6, row 10; `ORC-SFD2KHCML5.9d0105` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -3.113 kJ/mol (basis unstated) ± 0.046 | 1080 | liquid; _alloy: Li 0.98704, Sb 0.01296_ | experimental | [1] Li 2017 | Table 3, p. 6, row 4; `ORC-TR7IHMB45Q.ada3c0` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -0.722 kJ/mol (basis unstated) ± 0.011 | 1080 | liquid; _alloy: Li 0.99695, Sb 0.00305_ | experimental | [1] Li 2017 | Table 3, p. 6, row 1; `ORC-UZ6GVQRNMG.af5aa0` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -22.498 kJ/mol (basis unstated) ± 0.307 | 1080 | liquid; _alloy: Li 0.92803, Sb 0.07197_ | experimental | [1] Li 2017 | Table 3, p. 6, row 19; `ORC-VDMHT7PQXF.696606` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -29.355 kJ/mol (basis unstated) ± 0.417 | 1080 | liquid; _alloy: Li 0.90783, Sb 0.09217_ | experimental | [1] Li 2017 | Table 3, p. 6, row 23; `ORC-W5KI5UYQ5T.2d0e28` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -25.923 kJ/mol (basis unstated) ± 0.362 | 1080 | liquid; _alloy: Li 0.918, Sb 0.082_ | experimental | [1] Li 2017 | Table 3, p. 6, row 21; `ORC-WQG5YU7G5A.5b9e83` |  |
| Enthalpy of mixing; _printed: Δmix H_ | -19.416 kJ/mol (basis unstated) ± 0.289 | 1080 | liquid; _alloy: Li 0.93711, Sb 0.06289_ | experimental | [1] Li 2017 | Table 3, p. 6, row 17; `ORC-XNM6TYMKTE.e1aa4b` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -77.763 kJ/mol (basis unstated) ± 0.106 | 1181 | UNKNOWN; _alloy: Li 0.71964, Sb 0.28036_ | experimental | [1] Li 2017 | Table 9, p. 10, row 4; `ORC-72TKN3UOG6.8e6d92` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -79.602 kJ/mol (basis unstated) ± 0.077 | 1181 | UNKNOWN; _alloy: Li 0.73001, Sb 0.26999_ | experimental | [1] Li 2017 | Table 9, p. 10, row 3; `ORC-7DDF6Q6O6J.a13d6d` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -72.019 kJ/mol (basis unstated) ± 0.166 | 1181 | UNKNOWN; _alloy: Li 0.68715, Sb 0.31285_ | experimental | [1] Li 2017 | Table 9, p. 10, row 7; `ORC-B3Q76Q3ZNH.3e8bee` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -74.037 kJ/mol (basis unstated) ± 0.151 | 1181 | UNKNOWN; _alloy: Li 0.69875, Sb 0.30125_ | experimental | [1] Li 2017 | Table 9, p. 10, row 6; `ORC-B4MUY4LNTZ.6b353a` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -56.552 kJ/mol (basis unstated) ± 0.377 | 1181 | UNKNOWN; _alloy: Li 0.57009, Sb 0.42991_ | experimental | [1] Li 2017 | Table 9, p. 10, row 17; `ORC-DQJUDST43Z.23b999` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -67.471 kJ/mol (basis unstated) ± 0.238 | 1181 | UNKNOWN; _alloy: Li 0.66165, Sb 0.33835_ | experimental | [1] Li 2017 | Table 9, p. 10, row 9; `ORC-FLDGSBRCAK.4cf0d5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -61.062 kJ/mol (basis unstated) ± 0.326 | 1181 | UNKNOWN; _alloy: Li 0.61391, Sb 0.38609_ | experimental | [1] Li 2017 | Table 9, p. 10, row 13; `ORC-HP5KPJAVEK.9ecfe3` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -53.401 kJ/mol (basis unstated) ± 0.411 | 1181 | UNKNOWN; _alloy: Li 0.53885, Sb 0.46115_ | experimental | [1] Li 2017 | Table 9, p. 10, row 20; `ORC-JPQRPXNF4U.9e674a` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -75.907 kJ/mol (basis unstated) ± 0.135 | 1181 | UNKNOWN; _alloy: Li 0.70955, Sb 0.29045_ | experimental | [1] Li 2017 | Table 9, p. 10, row 5; `ORC-JSGTH7ITUZ.a20ce5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -69.59 kJ/mol (basis unstated) ± 0.206 | 1181 | UNKNOWN; _alloy: Li 0.67435, Sb 0.32565_ | experimental | [1] Li 2017 | Table 9, p. 10, row 8; `ORC-JWQOTXG67W.d3263a` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -52.378 kJ/mol (basis unstated) ± 0.423 | 1181 | UNKNOWN; _alloy: Li 0.52881, Sb 0.47119_ | experimental | [1] Li 2017 | Table 9, p. 10, row 21; `ORC-KCYHXEXQUE.c6b756` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -54.385 kJ/mol (basis unstated) ± 0.401 | 1181 | UNKNOWN; _alloy: Li 0.54897, Sb 0.45103_ | experimental | [1] Li 2017 | Table 9, p. 10, row 19; `ORC-KQZDNZX2AN.7d9243` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -63.558 kJ/mol (basis unstated) ± 0.297 | 1181 | UNKNOWN; _alloy: Li 0.63742, Sb 0.36258_ | experimental | [1] Li 2017 | Table 9, p. 10, row 11; `ORC-KSRPGL5RCD.08c1f4` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -51.395 kJ/mol (basis unstated) ± 0.433 | 1181 | UNKNOWN; _alloy: Li 0.51896, Sb 0.48104_ | experimental | [1] Li 2017 | Table 9, p. 10, row 22; `ORC-KUECU2UA5L.6cda4d` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -65.364 kJ/mol (basis unstated) ± 0.271 | 1181 | UNKNOWN; _alloy: Li 0.64937, Sb 0.35063_ | experimental | [1] Li 2017 | Table 9, p. 10, row 10; `ORC-LXN3IADT6Q.c6f1fe` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -55.45 kJ/mol (basis unstated) ± 0.389 | 1181 | UNKNOWN | experimental | [1] Li 2017 | Table 9, p. 10, row 18; `ORC-MWU2BSUVJ3.81dda5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -48.426 kJ/mol (basis unstated) ± 0.467 | 1181 | UNKNOWN; _alloy: Li 0.49013, Sb 0.50987_ | experimental | [1] Li 2017 | Table 9, p. 10, row 25; `ORC-NLSMYGH5C7.fc2d47` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -62.255 kJ/mol (basis unstated) ± 0.313 | 1181 | UNKNOWN; _alloy: Li 0.62556, Sb 0.37444_ | experimental | [1] Li 2017 | Table 9, p. 10, row 12; `ORC-OFFT32GZKH.eb17b8` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -49.424 kJ/mol (basis unstated) ± 0.455 | 1181 | UNKNOWN; _alloy: Li 0.49964, Sb 0.50036_ | experimental | [1] Li 2017 | Table 9, p. 10, row 24; `ORC-PQYY3PUVQT.6a1839` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -83.138 kJ/mol (basis unstated) ± 0.021 | 1181 | UNKNOWN; _alloy: Li 0.75, Sb 0.25_ | experimental | [1] Li 2017 | Table 9, p. 10, row 1; `ORC-QWK44342WG` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -59.979 kJ/mol (basis unstated) ± 0.337 | 1181 | UNKNOWN; _alloy: Li 0.60264, Sb 0.39736_ | experimental | [1] Li 2017 | Table 9, p. 10, row 14; `ORC-RODXZPLBGU.d0b4d5` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -57.685 kJ/mol (basis unstated) ± 0.364 | 1181 | UNKNOWN; _alloy: Li 0.58079, Sb 0.41921_ | experimental | [1] Li 2017 | Table 9, p. 10, row 16; `ORC-TWOHK3267T.acff3c` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -58.777 kJ/mol (basis unstated) ± 0.352 | 1181 | UNKNOWN; _alloy: Li 0.59158, Sb 0.40842_ | experimental | [1] Li 2017 | Table 9, p. 10, row 15; `ORC-UBFXLGUDF3.b80801` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -81.347 kJ/mol (basis unstated) ± 0.048 | 1181 | UNKNOWN; _alloy: Li 0.7401, Sb 0.2599_ | experimental | [1] Li 2017 | Table 9, p. 10, row 2; `ORC-W7NAOHTXW5.edde5a` |  |
| Enthalpy of mixing; _printed: ΔmixH_ | -50.386 kJ/mol (basis unstated) ± 0.445 | 1181 | UNKNOWN; _alloy: Li 0.50915, Sb 0.49085_ | experimental | [1] Li 2017 | Table 9, p. 10, row 23; `ORC-W7XE3PEZ6P.21c0d6` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -109.291 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.55589, Sb 0.44411_ | experimental | [1] Li 2017 | Table 4, p. 7, row 20; `ORC-2CKRUYB3DW.43ca08` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -100.034 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.39594, Sb 0.60406_ | experimental | [1] Li 2017 | Table 4, p. 7, row 12; `ORC-2XDURIRRQO.a5f91f` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -99.418 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.4195, Sb 0.5805_ | experimental | [1] Li 2017 | Table 4, p. 7, row 13; `ORC-3FN4FC4ZLX.146e41` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -121.401 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.57397, Sb 0.42603_ | experimental | [1] Li 2017 | Table 4, p. 7, row 21; `ORC-3IRQ6IJTIA.2fff85` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -62.929 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.22893, Sb 0.77107_ | experimental | [1] Li 2017 | Table 4, p. 7, row 6; `ORC-5BPQVDHI4K.58ba85` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -125.681 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.63699, Sb 0.36301_ | experimental | [1] Li 2017 | Table 4, p. 7, row 25; `ORC-5MMGHF6J5J.90eb91` |  |
| Partial enthalpy; _printed: Δmix H∞ (limiting partial molar enthalpy)_ | -89.5 kJ/mol (basis unstated) | 929 | liquid | experimental | [1] Li 2017 | Table 6, p. 8, row 3; `ORC-6R3RX7SGSR.c41677` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -127.029 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.62243, Sb 0.37757_ | experimental | [1] Li 2017 | Table 4, p. 7, row 24; `ORC-7CK67MT5ZO.aed6dc` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -122.198 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.59085, Sb 0.40915_ | experimental | [1] Li 2017 | Table 4, p. 7, row 22; `ORC-AEQLRV4BGJ.9fa04f` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -100.978 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.31949, Sb 0.68051_ | experimental | [1] Li 2017 | Table 4, p. 7, row 9; `ORC-C67CG5YGGA.0035d1` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -108.239 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.53919, Sb 0.46081_ | experimental | [1] Li 2017 | Table 4, p. 7, row 19; `ORC-GGZEKQU7S4.4bba77` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -105.307 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.44217, Sb 0.55783_ | experimental | [1] Li 2017 | Table 4, p. 7, row 14; `ORC-GV6USGVCSH.004af8` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -89.007 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.12088, Sb 0.87912_ | experimental | [1] Li 2017 | Table 4, p. 7, row 3; `ORC-HNMU5NSLAR.1133a3` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -108.678 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.52217, Sb 0.47783_ | experimental | [1] Li 2017 | Table 4, p. 7, row 18; `ORC-IQH7SQMS7C.cb0004` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -104.133 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.50387, Sb 0.49613_ | experimental | [1] Li 2017 | Table 4, p. 7, row 17; `ORC-KV65HOC7S2.675685` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -125.389 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.60678, Sb 0.39322_ | experimental | [1] Li 2017 | Table 4, p. 7, row 23; `ORC-LNA2VB3CTL.59d67a` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -86.929 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.195, Sb 0.805_ | experimental | [1] Li 2017 | Table 4, p. 7, row 5; `ORC-N6ZLIFXSFF.526ef1` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -89.957 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.08298, Sb 0.91702_ | experimental | [1] Li 2017 | Table 4, p. 7, row 2; `ORC-NGIDTXSSGC.3727a0` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -98.501 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.3465, Sb 0.6535_ | experimental | [1] Li 2017 | Table 4, p. 7, row 10; `ORC-NYQWQ3YHDC.24fe3b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -85.575 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.26107, Sb 0.73893_ | experimental | [1] Li 2017 | Table 4, p. 7, row 7; `ORC-ORCXUYWCRT.565681` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -101.137 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.37191, Sb 0.62809_ | experimental | [1] Li 2017 | Table 4, p. 7, row 11; `ORC-QX6HDKLOPI.233bde` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -104.386 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.29139, Sb 0.70861_ | experimental | [1] Li 2017 | Table 4, p. 7, row 8; `ORC-RK3S6OHT26.c36e11` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -103.37 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.46417, Sb 0.53583_ | experimental | [1] Li 2017 | Table 4, p. 7, row 15; `ORC-SIGVDMMRFD.3a0f61` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -103.253 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.48458, Sb 0.51542_ | experimental | [1] Li 2017 | Table 4, p. 7, row 16; `ORC-VLOVDRLDXP.108b0f` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -90.418 kJ/mol (basis unstated) | 929 | liquid; _alloy: Li 0.15795, Sb 0.84205_ | experimental | [1] Li 2017 | Table 4, p. 7, row 4; `ORC-W6ZAYH4AC4.190507` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Li_ | -89.742 kJ/mol (basis unstated) ± 2.688 | 929 | liquid; _alloy: Li 0.04221, Sb 0.95779_ | experimental | [1] Li 2017 | Table 4, p. 7, row 1; `ORC-YXN56HZPNM.51ed07` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -87.783 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.06354, Sb 0.93646_ | experimental | [1] Li 2017 | Table 5, p. 7, row 2; `ORC-27ENRZHFIH.42b0c6` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -101.936 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.13581, Sb 0.86419_ | experimental | [1] Li 2017 | Table 5, p. 7, row 4; `ORC-2QGHJJNDFX.d6b7e9` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 5.775 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.51975, Sb 0.48025_ | experimental | [1] Li 2017 | Table 7, p. 9, row 23; `ORC-2XJVL52ZZS.f23860` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.862 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.56853, Sb 0.43147_ | experimental | [1] Li 2017 | Table 7, p. 9, row 18; `ORC-324KCUAJTB.f12bbe` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -330.07 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.90916, Sb 0.09084_ | experimental | [1] Li 2017 | Table 2, p. 5, row 21; `ORC-366KWTOBRX.afce7e` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -105.447 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.55405, Sb 0.44595_ | experimental | [1] Li 2017 | Table 5, p. 7, row 20; `ORC-3BWGXP6SDT.3a593c` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 31.435 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.70319, Sb 0.29681_ | experimental | [1] Li 2017 | Table 7, p. 9, row 6; `ORC-3UMK4HZRHK.4d9d32` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -97.403 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.3607, Sb 0.6393_ | experimental | [1] Li 2017 | Table 5, p. 7, row 11; `ORC-3YALOHDNR3.7ae2a8` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -331.936 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.91809, Sb 0.08191_ | experimental | [1] Li 2017 | Table 2, p. 5, row 19; `ORC-4ZUNGQUW25.77a48c` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 28.445 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.71316, Sb 0.28684_ | experimental | [1] Li 2017 | Table 7, p. 9, row 5; `ORC-5BEUS7NSSP.8ca608` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -106.413 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.5196, Sb 0.4804_ | experimental | [1] Li 2017 | Table 5, p. 7, row 18; `ORC-5EULFO2SNI.12cf13` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -265.721 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.99647, Sb 0.00353_ | experimental | [1] Li 2017 | Table 2, p. 5, row 1; `ORC-5NZ545FAPJ.dca9e0` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -291.618 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.98906, Sb 0.01094_ | experimental | [1] Li 2017 | Table 2, p. 5, row 3; `ORC-5RTTGBYBLH.3878b8` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -86.383 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.09782, Sb 0.90218_ | experimental | [1] Li 2017 | Table 5, p. 7, row 3; `ORC-7CQZM6YFNQ.5ad670` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -94.805 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.17183, Sb 0.82817_ | experimental | [1] Li 2017 | Table 5, p. 7, row 5; `ORC-7IZSXRGLA5.878a2b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 28.373 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.58969, Sb 0.41031_ | experimental | [1] Li 2017 | Table 7, p. 9, row 16; `ORC-A23FUSO6HP.a771f9` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 23.707 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.73259, Sb 0.26741_ | experimental | [1] Li 2017 | Table 7, p. 9, row 3; `ORC-AD34SRG5AB.c3927e` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -129.377 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.6339, Sb 0.3661_ | experimental | [1] Li 2017 | Table 5, p. 7, row 25; `ORC-AGU7ATIYGJ.36b2ed` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -98.406 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.27444, Sb 0.72556_ | experimental | [1] Li 2017 | Table 5, p. 7, row 8; `ORC-ARISD7LQXQ.b3684d` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 32.957 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.6116, Sb 0.3884_ | experimental | [1] Li 2017 | Table 7, p. 9, row 14; `ORC-AUKWBMGA5C.982946` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -331.401 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.95653, Sb 0.04347_ | experimental | [1] Li 2017 | Table 2, p. 5, row 11; `ORC-BBVSGB56XG.341d34` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -98.978 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.38682, Sb 0.61318_ | experimental | [1] Li 2017 | Table 5, p. 7, row 12; `ORC-C64TM3NLHR.2882e9` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -106.331 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.56975, Sb 0.43025_ | experimental | [1] Li 2017 | Table 5, p. 7, row 21; `ORC-CJLV4LOPNF.1a50d5` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -330.611 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.9523, Sb 0.0477_ | experimental | [1] Li 2017 | Table 2, p. 5, row 12; `ORC-CK4YSGL7IJ.2de35b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 2.981 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.52902, Sb 0.47098_ | experimental | [1] Li 2017 | Table 7, p. 9, row 22; `ORC-CXYDLQ5DZE.4ed1a9` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -324.212 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.96075, Sb 0.03925_ | experimental | [1] Li 2017 | Table 2, p. 5, row 10; `ORC-DCQYNUYZK5.e4ed5e` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -91.192 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.02989, Sb 0.97011_ | experimental | [1] Li 2017 | Table 5, p. 7, row 1; `ORC-DGXTGV74FJ.cb2dd6` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -124.537 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.60082, Sb 0.39918_ | experimental | [1] Li 2017 | Table 5, p. 7, row 23; `ORC-DSM7RNGM22.f64a06` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -325.412 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.96892, Sb 0.03108_ | experimental | [1] Li 2017 | Table 2, p. 5, row 8; `ORC-ECIHSYUDRC.b0abc6` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -101.961 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.50076, Sb 0.49924_ | experimental | [1] Li 2017 | Table 5, p. 7, row 17; `ORC-EGWMVFTMZP.793aea` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -86.538 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.33276, Sb 0.66724_ | experimental | [1] Li 2017 | Table 5, p. 7, row 10; `ORC-EOL5JCK3PY.a629cf` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -330.369 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.94806, Sb 0.05194_ | experimental | [1] Li 2017 | Table 2, p. 5, row 13; `ORC-EZXO34WQZ3.a79e06` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.334 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.69267, Sb 0.30733_ | experimental | [1] Li 2017 | Table 7, p. 9, row 7; `ORC-F4A2JMFGJH.5b201d` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 31.883 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.60055, Sb 0.39945_ | experimental | [1] Li 2017 | Table 7, p. 9, row 15; `ORC-FIQ7BNHLFU.70202a` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -331.446 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.98125, Sb 0.01875_ | experimental | [1] Li 2017 | Table 2, p. 5, row 5; `ORC-GGF3AVZN5J.66cfcd` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -333.07 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.91368, Sb 0.08632_ | experimental | [1] Li 2017 | Table 2, p. 5, row 20; `ORC-JK5N7SNTIR.3891aa` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -126.419 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.61559, Sb 0.38441_ | experimental | [1] Li 2017 | Table 5, p. 7, row 24; `ORC-JNPKE2TTDJ.858615` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 30.936 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.64517, Sb 0.35483_ | experimental | [1] Li 2017 | Table 7, p. 9, row 11; `ORC-KLVT4YVNCO.62e3cb` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -331.535 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.94385, Sb 0.05615_ | experimental | [1] Li 2017 | Table 2, p. 5, row 14; `ORC-L33SX3YAL7.c0fa71` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 5.842 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.54823, Sb 0.45177_ | experimental | [1] Li 2017 | Table 7, p. 9, row 20; `ORC-MMQ6QORTQE.15acdb` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -323.753 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.96482, Sb 0.03518_ | experimental | [1] Li 2017 | Table 2, p. 5, row 9; `ORC-ND427AX3LA.3454f4` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 4.165 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.51057, Sb 0.48943_ | experimental | [1] Li 2017 | Table 7, p. 9, row 24; `ORC-OGB5BHFJ44.b4cdaf` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.543 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.74165, Sb 0.25835_ | experimental | [1] Li 2017 | Table 7, p. 9, row 2; `ORC-PCZK7MQCTV.992b0d` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -100.559 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.4805, Sb 0.5195_ | experimental | [1] Li 2017 | Table 5, p. 7, row 16; `ORC-PJ7QENEB33.18d5f4` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -89.342 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.20836, Sb 0.79164_ | experimental | [1] Li 2017 | Table 5, p. 7, row 6; `ORC-PT3AK5E5VQ.1d0855` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -334.908 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.89506, Sb 0.10494_ | experimental | [1] Li 2017 | Table 2, p. 5, row 24; `ORC-QC5K7ODIQI.2bfb53` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -315.597 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.9852, Sb 0.0148_ | experimental | [1] Li 2017 | Table 2, p. 5, row 4; `ORC-QMOW2L7IX7.633212` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -334.172 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.93524, Sb 0.06476_ | experimental | [1] Li 2017 | Table 2, p. 5, row 16; `ORC-QOCRQBJDUB.adcdb2` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -330.095 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.90458, Sb 0.09542_ | experimental | [1] Li 2017 | Table 2, p. 5, row 22; `ORC-QVRKZ3JDES.567c35` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -336.929 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.8998, Sb 0.1002_ | experimental | [1] Li 2017 | Table 2, p. 5, row 23; `ORC-QXNLTOYRPC.81381e` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -105.521 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.53722, Sb 0.46278_ | experimental | [1] Li 2017 | Table 5, p. 7, row 19; `ORC-REX4O7CVVS.085005` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -98.614 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.30413, Sb 0.69587_ | experimental | [1] Li 2017 | Table 5, p. 7, row 9; `ORC-RJVTZB7JFG.d4a994` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.051 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.66854, Sb 0.33146_ | experimental | [1] Li 2017 | Table 7, p. 9, row 9; `ORC-RLTCUJXUAN.82e1a1` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -327.129 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.93095, Sb 0.06905_ | experimental | [1] Li 2017 | Table 2, p. 5, row 17; `ORC-S2UL3AKO7G.be68a8` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 8.76 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.5582, Sb 0.4418_ | experimental | [1] Li 2017 | Table 7, p. 9, row 19; `ORC-SCT4AX4CNS.279052` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -103.397 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.4587, Sb 0.5413_ | experimental | [1] Li 2017 | Table 5, p. 7, row 15; `ORC-TSSLBQG7IF.d5e37a` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 29.499 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.7234, Sb 0.2766_ | experimental | [1] Li 2017 | Table 7, p. 9, row 4; `ORC-U46GIDWBAC.d4533e` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.879 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.62282, Sb 0.37718_ | experimental | [1] Li 2017 | Table 7, p. 9, row 13; `ORC-U4AXTSYQAU.3098c8` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -92.833 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.24245, Sb 0.75755_ | experimental | [1] Li 2017 | Table 5, p. 7, row 7; `ORC-U6YCP2D4CE.fdf20f` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -101.519 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.43499, Sb 0.56501_ | experimental | [1] Li 2017 | Table 5, p. 7, row 14; `ORC-U76E3N3IBK.cefb01` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -283.695 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.99287, Sb 0.00713_ | experimental | [1] Li 2017 | Table 2, p. 5, row 2; `ORC-UCAWQ7TJ6P.dcefa3` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -333.151 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.92669, Sb 0.07331_ | experimental | [1] Li 2017 | Table 2, p. 5, row 18; `ORC-V3ZLX7NUVW.e10e5a` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -103.55 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.41167, Sb 0.58833_ | experimental | [1] Li 2017 | Table 5, p. 7, row 13; `ORC-VCFZCCR356.2573aa` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -325.746 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.97716, Sb 0.02284_ | experimental | [1] Li 2017 | Table 2, p. 5, row 6; `ORC-VEF6TLJI5M.7c93df` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 5.769 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.50104, Sb 0.49896_ | experimental | [1] Li 2017 | Table 7, p. 9, row 25; `ORC-VF4OBQG2UZ.7ef2af` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -327.303 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.97303, Sb 0.02697_ | experimental | [1] Li 2017 | Table 2, p. 5, row 7; `ORC-W5YFYFLRKV.6dfb43` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 13.941 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.53851, Sb 0.46149_ | experimental | [1] Li 2017 | Table 7, p. 9, row 21; `ORC-WLL5KIGXCE.efe3bf` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 25.284 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.65666, Sb 0.34334_ | experimental | [1] Li 2017 | Table 7, p. 9, row 10; `ORC-WNJNP47VAM.61b15e` |  |
| Partial enthalpy; _printed: ΔmixH̄Sb_ | -332.043 kJ/mol-atom ± 3724 | 979 | UNKNOWN; _alloy: Li 0.93955, Sb 0.06045_ | experimental | [1] Li 2017 | Table 2, p. 5, row 15; `ORC-XQBHD62QNB.9edb91` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.352 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.63408, Sb 0.36592_ | experimental | [1] Li 2017 | Table 7, p. 9, row 12; `ORC-YF5XFHR4R5.641cb1` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 32.448 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.68064, Sb 0.31936_ | experimental | [1] Li 2017 | Table 7, p. 9, row 8; `ORC-YFEPYD4OTH.943b41` |  |
| Partial enthalpy; _printed: ΔmixH_Li_ | -114.327 kJ/mol (basis unstated) ± 1.268 | 979 | UNKNOWN; _alloy: Li 0.58518, Sb 0.41482_ | experimental | [1] Li 2017 | Table 5, p. 7, row 22; `ORC-YGRYUHWU3K.d6de22` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 27.812 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.57897, Sb 0.42103_ | experimental | [1] Li 2017 | Table 7, p. 9, row 17; `ORC-ZGOVESY4GA.6f73ae` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | 7.648 kJ/mol (basis unstated) | 979 | UNKNOWN; _alloy: Li 0.49161, Sb 0.50839_ | experimental | [1] Li 2017 | Table 7, p. 9, row 26; `ORC-ZOINEUQ6R5.099f7b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -330.07 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.91142, Sb 0.08858_ | experimental | [1] Li 2017 | Table 2, p. 5, row 21; `ORC-366KWTOBRX.bf1088` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -331.936 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.92239, Sb 0.07761_ | experimental | [1] Li 2017 | Table 2, p. 5, row 19; `ORC-4ZUNGQUW25.8f963d` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -265.721 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.99823, Sb 0.00177_ | experimental | [1] Li 2017 | Table 2, p. 5, row 1; `ORC-5NZ545FAPJ.b13d31` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -291.618 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.99096, Sb 0.00904_ | experimental | [1] Li 2017 | Table 2, p. 5, row 3; `ORC-5RTTGBYBLH.a3d807` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -331.401 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.95864, Sb 0.04136_ | experimental | [1] Li 2017 | Table 2, p. 5, row 11; `ORC-BBVSGB56XG.54082c` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -330.611 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.95441, Sb 0.04559_ | experimental | [1] Li 2017 | Table 2, p. 5, row 12; `ORC-CK4YSGL7IJ.5fb802` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -324.212 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.96278, Sb 0.03722_ | experimental | [1] Li 2017 | Table 2, p. 5, row 10; `ORC-DCQYNUYZK5.7c3773` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -325.412 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.97098, Sb 0.02902_ | experimental | [1] Li 2017 | Table 2, p. 5, row 8; `ORC-ECIHSYUDRC.b45549` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -330.369 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.95018, Sb 0.04982_ | experimental | [1] Li 2017 | Table 2, p. 5, row 13; `ORC-EZXO34WQZ3.e53fc9` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -331.446 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.98323, Sb 0.01677_ | experimental | [1] Li 2017 | Table 2, p. 5, row 5; `ORC-GGF3AVZN5J.017432` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -333.07 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.91588, Sb 0.08412_ | experimental | [1] Li 2017 | Table 2, p. 5, row 20; `ORC-JK5N7SNTIR.46755d` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -331.535 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.94596, Sb 0.05404_ | experimental | [1] Li 2017 | Table 2, p. 5, row 14; `ORC-L33SX3YAL7.a54e2b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -323.753 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.96687, Sb 0.03313_ | experimental | [1] Li 2017 | Table 2, p. 5, row 9; `ORC-ND427AX3LA.9b3cf8` |  |
| Partial enthalpy; _printed: Δmix H∞ (limiting partial molar enthalpy)_ | -88 kJ/mol (basis unstated) | 979 | liquid | experimental | [1] Li 2017 | Table 6, p. 8, row 2; `ORC-O6YACCZNTR.a34915` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -334.908 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.89743, Sb 0.10257_ | experimental | [1] Li 2017 | Table 2, p. 5, row 24; `ORC-QC5K7ODIQI.7a68c1` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -315.597 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.98713, Sb 0.01287_ | experimental | [1] Li 2017 | Table 2, p. 5, row 4; `ORC-QMOW2L7IX7.b8a8cb` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -334.172 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.93739, Sb 0.06261_ | experimental | [1] Li 2017 | Table 2, p. 5, row 16; `ORC-QOCRQBJDUB.3fbb0c` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -330.095 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.90687, Sb 0.09313_ | experimental | [1] Li 2017 | Table 2, p. 5, row 22; `ORC-QVRKZ3JDES.d9d44d` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -336.929 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.90219, Sb 0.09781_ | experimental | [1] Li 2017 | Table 2, p. 5, row 23; `ORC-QXNLTOYRPC.ab32c8` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -327.129 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.93309, Sb 0.06691_ | experimental | [1] Li 2017 | Table 2, p. 5, row 17; `ORC-S2UL3AKO7G.cd1c5a` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -283.695 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.99467, Sb 0.00533_ | experimental | [1] Li 2017 | Table 2, p. 5, row 2; `ORC-UCAWQ7TJ6P.054e2b` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -333.151 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.92882, Sb 0.07118_ | experimental | [1] Li 2017 | Table 2, p. 5, row 18; `ORC-V3ZLX7NUVW.359cef` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -325.746 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.9792, Sb 0.0208_ | experimental | [1] Li 2017 | Table 2, p. 5, row 6; `ORC-VEF6TLJI5M.03546c` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -327.303 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.97509, Sb 0.02491_ | experimental | [1] Li 2017 | Table 2, p. 5, row 7; `ORC-W5YFYFLRKV.d9b628` |  |
| Partial enthalpy; _printed: ΔmixH̄\_Sb_ | -332.043 kJ/mol (basis unstated) | 979 | liquid; _alloy: Li 0.9417, Sb 0.0583_ | experimental | [1] Li 2017 | Table 2, p. 5, row 15; `ORC-XQBHD62QNB.b547cc` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 3.726 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.57085, Sb 0.42915_ | experimental | [1] Li 2017 | Table 8, p. 9, row 19; `ORC-2SV7LOJBVG` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 30.817 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.66319, Sb 0.33681_ | experimental | [1] Li 2017 | Table 8, p. 9, row 10; `ORC-3GI2I3PO2W` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 36.846 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.62236, Sb 0.37764_ | experimental | [1] Li 2017 | Table 8, p. 9, row 14; `ORC-3OTZ6RNTE7` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 30.936 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.653, Sb 0.347_ | experimental | [1] Li 2017 | Table 8, p. 9, row 11; `ORC-3WJTOR3PKT` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 30.465 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.72312, Sb 0.27688_ | experimental | [1] Li 2017 | Table 8, p. 9, row 4; `ORC-4SRFSPBCHS` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 34.09 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.7138, Sb 0.2862_ | experimental | [1] Li 2017 | Table 8, p. 9, row 5; `ORC-4TCC65SWNX` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 39.641 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.64289, Sb 0.35711_ | experimental | [1] Li 2017 | Table 8, p. 9, row 12; `ORC-56F7RIBT7Y` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 7.347 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.55162, Sb 0.44838_ | experimental | [1] Li 2017 | Table 8, p. 9, row 21; `ORC-7RRMZAOWIV` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 20.591 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.74165, Sb 0.25835_ | experimental | [1] Li 2017 | Table 8, p. 9, row 2; `ORC-AO7JOMTDVA` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 6.043 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.51419, Sb 0.48581_ | experimental | [1] Li 2017 | Table 8, p. 9, row 25; `ORC-BBCQZMUVVH` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 7.779 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.58085, Sb 0.41915_ | experimental | [1] Li 2017 | Table 8, p. 9, row 18; `ORC-F4JI53EVBN` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 3.274 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.50513, Sb 0.49487_ | experimental | [1] Li 2017 | Table 8, p. 9, row 26; `ORC-FF3JL6HGGQ` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 3.941 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.56115, Sb 0.43885_ | experimental | [1] Li 2017 | Table 8, p. 9, row 20; `ORC-HM76DRBKQX` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 22.811 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.60156, Sb 0.39844_ | experimental | [1] Li 2017 | Table 8, p. 9, row 16; `ORC-HS5KTCD5O7` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 4.383 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.52335, Sb 0.47665_ | experimental | [1] Li 2017 | Table 8, p. 9, row 24; `ORC-IFF3QDMYWW` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 42.092 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.63271, Sb 0.36729_ | experimental | [1] Li 2017 | Table 8, p. 9, row 13; `ORC-JJZFUCVQ55` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 36.827 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.70433, Sb 0.29567_ | experimental | [1] Li 2017 | Table 8, p. 9, row 6; `ORC-L7SNPPAE6B` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 44.572 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.69447, Sb 0.30553_ | experimental | [1] Li 2017 | Table 8, p. 9, row 7; `ORC-P5E37Z7JGD` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 50.62 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.67356, Sb 0.32644_ | experimental | [1] Li 2017 | Table 8, p. 9, row 9; `ORC-PFGQR43POF` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 4.235 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.59114, Sb 0.40886_ | experimental | [1] Li 2017 | Table 8, p. 9, row 17; `ORC-RQAI2KDMGO` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 5.752 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.5327, Sb 0.4673_ | experimental | [1] Li 2017 | Table 8, p. 9, row 23; `ORC-T7KGQHSRYO` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 4.14 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.54208, Sb 0.45792_ | experimental | [1] Li 2017 | Table 8, p. 9, row 22; `ORC-UGQSL7Z42A` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 39.548 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.61195, Sb 0.38805_ | experimental | [1] Li 2017 | Table 8, p. 9, row 15; `ORC-VQRX5QQXYC` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 33.546 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.73248, Sb 0.26752_ | experimental | [1] Li 2017 | Table 8, p. 9, row 3; `ORC-WEQ6IZWYM4` |  |
| Partial enthalpy; _printed: ΔmixH_Sb_ | 40.805 kJ/mol-atom | 1080 | UNKNOWN; _alloy: Li 0.68386, Sb 0.31614_ | experimental | [1] Li 2017 | Table 8, p. 9, row 8; `ORC-ZKFLQJXDDG` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -337.324 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.92311, Sb 0.07689_ | experimental | [1] Li 2017 | Table 3, p. 6, row 20; `ORC-2BQHK4P4FL.2ca0cf` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -333.807 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.96895, Sb 0.03105_ | experimental | [1] Li 2017 | Table 3, p. 6, row 9; `ORC-2C53JADKMD.934192` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -241.516 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.99046, Sb 0.00954_ | experimental | [1] Li 2017 | Table 3, p. 6, row 3; `ORC-5P37AKXDJA.dfbd1f` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -267.115 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.98352, Sb 0.01648_ | experimental | [1] Li 2017 | Table 3, p. 6, row 5; `ORC-5QHCOCHWGW.540211` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -339.241 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.89744, Sb 0.10256_ | experimental | [1] Li 2017 | Table 3, p. 6, row 25; `ORC-5ZU4LEKRXD.c14908` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -331.514 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.94118, Sb 0.05882_ | experimental | [1] Li 2017 | Table 3, p. 6, row 16; `ORC-622PGZM3T2.5bf721` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -336.921 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.9454, Sb 0.0546_ | experimental | [1] Li 2017 | Table 3, p. 6, row 15; `ORC-63WJIQMRVL.300736` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -341.297 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.9612, Sb 0.0388_ | experimental | [1] Li 2017 | Table 3, p. 6, row 11; `ORC-A7W3KER6E5.9ad35a` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -322.63 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.97647, Sb 0.02353_ | experimental | [1] Li 2017 | Table 3, p. 6, row 7; `ORC-AXC7ARC6Y6.69d3ea` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -289.491 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.98001, Sb 0.01999_ | experimental | [1] Li 2017 | Table 3, p. 6, row 6; `ORC-CC4ZATIHZY.c67045` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -328.055 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.93296, Sb 0.06704_ | experimental | [1] Li 2017 | Table 3, p. 6, row 18; `ORC-GV7ELY7DVL.a35eae` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -331.473 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.9728, Sb 0.0272_ | experimental | [1] Li 2017 | Table 3, p. 6, row 8; `ORC-IT7YSQMHF6.34f390` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -333.448 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.91292, Sb 0.08708_ | experimental | [1] Li 2017 | Table 3, p. 6, row 22; `ORC-LS2LFPX7UP.d69a5a` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -334.11 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.94958, Sb 0.05042_ | experimental | [1] Li 2017 | Table 3, p. 6, row 14; `ORC-LTGY7ET35B.62e266` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -238.638 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.99376, Sb 0.00624_ | experimental | [1] Li 2017 | Table 3, p. 6, row 2; `ORC-N4R4VXHYYS.f09bd2` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -333.126 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.95731, Sb 0.04269_ | experimental | [1] Li 2017 | Table 3, p. 6, row 12; `ORC-OWJSHDZEA6.038b44` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -335.362 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.95344, Sb 0.04656_ | experimental | [1] Li 2017 | Table 3, p. 6, row 13; `ORC-P5GGFOWMDH.9df34c` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -337.966 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.90271, Sb 0.09729_ | experimental | [1] Li 2017 | Table 3, p. 6, row 24; `ORC-PRVEMNGLQK.06d7f2` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -330.973 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.96508, Sb 0.03492_ | experimental | [1] Li 2017 | Table 3, p. 6, row 10; `ORC-SFD2KHCML5.32924f` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -243.555 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.98704, Sb 0.01296_ | experimental | [1] Li 2017 | Table 3, p. 6, row 4; `ORC-TR7IHMB45Q.197f14` |  |
| Partial enthalpy; _printed: Δmix H∞ (limiting partial molar enthalpy)_ | -238 kJ/mol (basis unstated) | 1080 | liquid | experimental | [1] Li 2017 | Table 6, p. 8, row 1; `ORC-UGSGCTM3FJ.8eed74` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -236.477 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.99695, Sb 0.00305_ | experimental | [1] Li 2017 | Table 3, p. 6, row 1; `ORC-UZ6GVQRNMG.2e3239` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -345.609 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.92803, Sb 0.07197_ | experimental | [1] Li 2017 | Table 3, p. 6, row 19; `ORC-VDMHT7PQXF.2d7dfd` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -337.959 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.90783, Sb 0.09217_ | experimental | [1] Li 2017 | Table 3, p. 6, row 23; `ORC-W5KI5UYQ5T.a8d282` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -341.361 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.918, Sb 0.082_ | experimental | [1] Li 2017 | Table 3, p. 6, row 21; `ORC-WQG5YU7G5A.e8dfe1` |  |
| Partial enthalpy; _printed: Δmix H̄\_Sb_ | -327.71 kJ/mol (basis unstated) ± 4.562 | 1080 | liquid; _alloy: Li 0.93711, Sb 0.06289_ | experimental | [1] Li 2017 | Table 3, p. 6, row 17; `ORC-XNM6TYMKTE.4869e3` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 49.848 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.71964, Sb 0.28036_ | experimental | [1] Li 2017 | Table 9, p. 10, row 4; `ORC-72TKN3UOG6.6c4d80` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 46.644 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.73001, Sb 0.26999_ | experimental | [1] Li 2017 | Table 9, p. 10, row 3; `ORC-7DDF6Q6O6J.44cbf1` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 48.679 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.68715, Sb 0.31285_ | experimental | [1] Li 2017 | Table 9, p. 10, row 7; `ORC-B3Q76Q3ZNH.801632` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 46.948 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.69875, Sb 0.30125_ | experimental | [1] Li 2017 | Table 9, p. 10, row 6; `ORC-B4MUY4LNTZ.abd5cf` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 3.782 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.57009, Sb 0.42991_ | experimental | [1] Li 2017 | Table 9, p. 10, row 17; `ORC-DQJUDST43Z.94ba7b` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 42.924 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.66165, Sb 0.33835_ | experimental | [1] Li 2017 | Table 9, p. 10, row 9; `ORC-FLDGSBRCAK.657e4d` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.813 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.61391, Sb 0.38609_ | experimental | [1] Li 2017 | Table 9, p. 10, row 13; `ORC-HP5KPJAVEK.24dc77` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | -0.962 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.53885, Sb 0.46115_ | experimental | [1] Li 2017 | Table 9, p. 10, row 20; `ORC-JPQRPXNF4U.9b75e7` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 54.57 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.70955, Sb 0.29045_ | experimental | [1] Li 2017 | Table 9, p. 10, row 5; `ORC-JSGTH7ITUZ.fa0180` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 58.423 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.67435, Sb 0.32565_ | experimental | [1] Li 2017 | Table 9, p. 10, row 8; `ORC-JWQOTXG67W.85ee38` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.526 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.52881, Sb 0.47119_ | experimental | [1] Li 2017 | Table 9, p. 10, row 21; `ORC-KCYHXEXQUE.dda2b5` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.217 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.54897, Sb 0.45103_ | experimental | [1] Li 2017 | Table 9, p. 10, row 19; `ORC-KQZDNZX2AN.1318e5` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 32.836 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.63742, Sb 0.36258_ | experimental | [1] Li 2017 | Table 9, p. 10, row 11; `ORC-KSRPGL5RCD.06fb6e` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 0.374 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.51896, Sb 0.48104_ | experimental | [1] Li 2017 | Table 9, p. 10, row 22; `ORC-KUECU2UA5L.c6c436` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 46.033 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.64937, Sb 0.35063_ | experimental | [1] Li 2017 | Table 9, p. 10, row 10; `ORC-LXN3IADT6Q.ef868b` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 2.703 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN | experimental | [1] Li 2017 | Table 9, p. 10, row 18; `ORC-MWU2BSUVJ3.a9b754` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 2.962 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.49013, Sb 0.50987_ | experimental | [1] Li 2017 | Table 9, p. 10, row 25; `ORC-NLSMYGH5C7.5360fd` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 6.405 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.62556, Sb 0.37444_ | experimental | [1] Li 2017 | Table 9, p. 10, row 12; `ORC-OFFT32GZKH.fd4f4e` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.154 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.49964, Sb 0.50036_ | experimental | [1] Li 2017 | Table 9, p. 10, row 24; `ORC-PQYY3PUVQT.d9f854` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | -2.043 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.60264, Sb 0.39736_ | experimental | [1] Li 2017 | Table 9, p. 10, row 14; `ORC-RODXZPLBGU.feeafc` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.061 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.58079, Sb 0.41921_ | experimental | [1] Li 2017 | Table 9, p. 10, row 16; `ORC-TWOHK3267T.8eec2a` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 5.531 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.59158, Sb 0.40842_ | experimental | [1] Li 2017 | Table 9, p. 10, row 15; `ORC-UBFXLGUDF3.4419d6` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 52.549 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.7401, Sb 0.2599_ | experimental | [1] Li 2017 | Table 9, p. 10, row 2; `ORC-W7NAOHTXW5.cae446` |  |
| Partial enthalpy; _printed: ΔmixH¯Sb_ | 1.952 kJ/mol (basis unstated) ± 1.427 | 1181 | UNKNOWN; _alloy: Li 0.50915, Sb 0.49085_ | experimental | [1] Li 2017 | Table 9, p. 10, row 23; `ORC-W7XE3PEZ6P.12f9d0` |  |

## Sources

Reporting papers the values were read from (a value cited from another work names that work in its row).

1. D. Li, A. Beutl, H. Flandorfer, D.M. Cupid, The Li-Sb phase diagram part II: Calorimetry and thermodynamic assessment, Journal of Alloys and Compounds 701, 186-199 (2017). [doi:10.1016/j.jallcom.2016.12.399](https://doi.org/10.1016/j.jallcom.2016.12.399)
2. Fan Zhang, Shuhong Liu, Jianchuan Wang, Yong Du, Lixian Sun, Experimental investigation and thermodynamic assessment of the Li-Sb system, Calphad 57, 28-36 (2017). [doi:10.1016/j.calphad.2017.01.005](https://doi.org/10.1016/j.calphad.2017.01.005)

## Please cite

- R. Arróyave, J. Saal, D. Shin, ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature (version 2026.10; Version 1, machine-extracted), Zenodo (2026). https://doi.org/10.5281/zenodo.23735569
- R. Arróyave, J. Saal, D. Shin, ORCHID-Diagrams: calculated binary phase diagrams (version 2026.10), Zenodo (2026). https://doi.org/10.5281/zenodo.23735859
- R. Arróyave, J. Saal, D. Shin, ORCHID-Hulls: binary convex hulls (Materials Project, OQMD, assessed CALPHAD) (version 2026.10), Zenodo (2026). https://doi.org/10.5281/zenodo.23735891
- R. Arróyave, J. Saal, D. Shin, ORCHID data: umbrella record of the ORCHID datasets (version 2026.10; Version 1, machine-extracted), Zenodo (2026). https://doi.org/10.5281/zenodo.23736065

Also cite the original source of every value you use (paper_citation / paper_doi, and cited_dois for values the paper cites from earlier work); B. Hallstedt, The SGTE collection of binary datasets, Calphad 89 (2025) 102833, https://doi.org/10.1016/j.calphad.2025.102833 (CC BY 4.0), and the original assessment named in each file; A. Jain et al., The Materials Project: A materials genome approach to accelerating materials innovation, APL Materials 1 (2013) 011002, https://doi.org/10.1063/1.4812323 (CC BY 4.0); J. E. Saal et al., JOM 65 (2013) 1501, https://doi.org/10.1007/s11837-013-0755-4 and S. Kirklin et al., npj Comput. Mater. 1 (2015) 15010, https://doi.org/10.1038/npjcompumats.2015.10 (CC BY 4.0).

Version 1, machine-extracted: values were read by language-model readers constrained to quote their source and checked automatically, and the release was then audited on the printed pages by adversarial audits, an independent second review of fit-facing records and a preliminary human review of a frozen sample. Flags such as accepted and ESPEI-ready record screening results, not certification; known issues are listed in the release notes.

```bibtex
@misc{orchid_literature_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23735569},
  url       = {https://doi.org/10.5281/zenodo.23735569},
  note      = {Version 1, machine-extracted}
}

@misc{orchid_phase_diagrams_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID-Diagrams: calculated binary phase diagrams}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23735859},
  url       = {https://doi.org/10.5281/zenodo.23735859}
}

@misc{orchid_hulls_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID-Hulls: binary convex hulls (Materials Project, OQMD, assessed CALPHAD)}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23735891},
  url       = {https://doi.org/10.5281/zenodo.23735891}
}

@misc{orchid_data_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID data: umbrella record of the ORCHID datasets}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23736065},
  url       = {https://doi.org/10.5281/zenodo.23736065},
  note      = {Version 1, machine-extracted}
}
```

---

Derived data CC BY 4.0 ([licence](https://creativecommons.org/licenses/by/4.0/)): cite ORCHID ([CITATION.cff](https://data.orchid-project.org/CITATION.cff)) and the original sources. Quotes are short excerpts kept so that each value can be checked; they remain under the publishers' copyright and are not relicensed. Source papers, page images and full text are not redistributed. Field reference: [SCHEMA.md](https://data.orchid-project.org/literature/SCHEMA.md). Machine-readable guide: [llms.txt](https://data.orchid-project.org/llms.txt). Found an error? The report link of a value (Markdown: its id, ORC-..., in the Location column) opens a pre-filled GitHub issue, https://github.com/orchid-calphad/orchid-data/issues/new?template=report-value-error.yml&record_id=\<id>, carrying only the record id, source and value; [how to contribute](https://orchid-project.org/contribute/).