S system

401 accepted literature values from 4 paper(s) (experimental 32, DFT 369); 0 calculated phase diagram(s).

Data: JSON · CSV · interactive explorer · papers (bibliography) · Markdown

Accepted values by evidence class
Evidence class	Values
experimental	32
DFT	369

Accepted values by property group
Property group	Values
crystal structure	396
other property	5

Other properties

Crystal structure (396)

Crystal structure, S system
Property	Value	T (K)	Phases / composition	Class	Source	Location
Lattice a	11.068 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 61 report
Lattice a	10.981 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 73 report
Lattice a	10.434 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 85 report
Lattice a	10.45 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 91 report
Lattice a	10.909 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 103 report
Lattice a	10.232 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 19 report
Lattice a	10.823 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 67 report
Lattice a	10.971 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 37 report
Lattice a	11.063 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 79 report
Lattice a	10.198 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 7 report
Lattice a	10.087 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 13 report
Lattice a	10.378 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 97 report
Lattice a	10.24 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 1 report
Lattice a	10.147 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 31 report
Lattice a	11.042 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 55 report
Lattice a	10.887 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 43 report
Lattice a	10.21 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 25 report
Lattice a	10.735 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 49 report
Lattice a	9.928 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 50 report
Lattice a	9.697 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 86 report
Lattice a	9.142 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 14 report
Lattice a	11.786 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 104 report
Lattice a	9.328 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 2 report
Lattice a	10.047 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 68 report
Lattice a	10.678 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 56 report
Lattice a	9.287 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 26 report
Lattice a	9.155 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 32 report
Lattice a	10.564 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 62 report
Lattice a	10.539 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 44 report
Lattice a	9.32 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 20 report
Lattice a	10.479 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 38 report
Lattice a	9.6653 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 92 report
Lattice a	9.245 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 8 report
Lattice a	10.189 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 80 report
Lattice a	9.453 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 98 report
Lattice a	10.324 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 74 report
Lattice a	9.502 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 63 report
Lattice a	7.934 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 9 report
Lattice a	7.68 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 15 report
Lattice a	8.799 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 69 report
Lattice a	8.455 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 93 report
Lattice a	9.082 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 75 report
Lattice a	9.288 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 45 report
Lattice a	10.886 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 105 report
Lattice a	8.004 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 21 report
Lattice a	8.018 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 3 report
Lattice a	8.971 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 81 report
Lattice a	7.962 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 27 report
Lattice a	8.533 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 87 report
Lattice a	9.586 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 39 report
Lattice a	8.553 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 51 report
Lattice a	7.826 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 33 report
Lattice a	9.469 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 57 report
Lattice a	8.161 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 99 report
Lattice a	16.227 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 76 report
Lattice a	15.032 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 94 report
Lattice a	16.666 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 40 report
Lattice a	15.02 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 88 report
Lattice a	14.153 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 34 report
Lattice a	16.599 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 58 report
Lattice a	14.627 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 100 report
Lattice a	15.378 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 52 report
Lattice a	15.636 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 70 report
Lattice a	14.355 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 28 report
Lattice a	16.49 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 64 report
Lattice a	13.954 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 16 report
Lattice a	16.297 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 46 report
Lattice a	17.547 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 106 report
Lattice a	15.788 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 82 report
Lattice a	14.301 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 10 report
Lattice a	14.436 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 4 report
Lattice a	14.422 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 22 report
Lattice a	10.255 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 35 report
Lattice a	11.282 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 71 report
Lattice a	10.521 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 23 report
Lattice a	11.127 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 89 report
Lattice a	11.104 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 53 report
Lattice a	10.6 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 101 report
Lattice a	12.007 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 59 report
Lattice a	12.887 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 107 report
Lattice a	10.983 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 95 report
Lattice a	12.183 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 41 report
Lattice a	10.143 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 17 report
Lattice a	11.369 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 83 report
Lattice a	10.384 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 11 report
Lattice a	11.961 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 65 report
Lattice a	11.798 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 47 report
Lattice a	10.53 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 5 report
Lattice a	10.455 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 29 report
Lattice a	11.598 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 77 report
Lattice a	10.823 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 72 report
Lattice a	9.685 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 36 report
Lattice a	9.936 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 24 report
Lattice a	11.285 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 78 report
Lattice a	9.958 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 6 report
Lattice a	12.202 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 42 report
Lattice a	13.558 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 108 report
Lattice a	10.096 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 102 report
Lattice a	10.641 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 54 report
Lattice a	11.911 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 66 report
Lattice a	11.669 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 48 report
Lattice a	10.526 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 90 report
Lattice a	11.951 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 60 report
Lattice a	9.818 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 12 report
Lattice a	10.523 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 96 report
Lattice a	9.886 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 30 report
Lattice a	11.083 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 84 report
Lattice a	9.489 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 18 report
Lattice a	1.092 Å	298.15	(S) alloy: S 1	experimental	[2] Chen 2022 cites King 1981	Table I, p. 2, row 9 report
Lattice a	1.0465 Å	298.15	(αS) alloy: S 1	experimental	[3] Shi 2019 cites King 1981 doi	Table 2, p. 3, row 2 report
Lattice a	1.092 Å	298.15	(βS) alloy: S 1	experimental	[3] Shi 2019 cites Reid 2006 doi	Table 2, p. 3, row 3 report
Lattice a	10.9 Å	298.15	S.hR6	experimental	[1] Hu 2010 cites Donnay 1955 doi	Table A.2, p. 6, row 109 report
Lattice a	9.68 Å	298.15	S.mP28	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 110 report
Lattice a	8.442 Å	298.15	S.mP32	experimental	[1] Hu 2010 cites Watanabe 1974 doi	Table A.2, p. 6, row 111 report
Lattice a	15.096 Å	298.15	S.mP56	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 112 report
Lattice a	11.02 Å	298.15	S.mP64	experimental	[1] Hu 2010 cites Sands 1965 doi	Table A.2, p. 6, row 113 report
Lattice a	10.465 Å	298.15	S.oF128	experimental	[1] Hu 2010 cites Rettig 1987 doi	Table A.2, p. 6, row 114 report
Lattice b	7.849 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 50 report
Lattice b	7.673 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 86 report
Lattice b	7.344 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 14 report
Lattice b	9.063 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 104 report
Lattice b	7.454 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 2 report
Lattice b	7.896 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 68 report
Lattice b	8.265 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 56 report
Lattice b	7.424 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 26 report
Lattice b	7.35 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 32 report
Lattice b	8.304 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 62 report
Lattice b	8.138 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 44 report
Lattice b	7.47 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 20 report
Lattice b	8.182 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 38 report
Lattice b	7.66 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 92 report
Lattice b	7.384 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 8 report
Lattice b	7.827 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 80 report
Lattice b	7.502 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 98 report
Lattice b	8.089 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 74 report
Lattice b	13.822 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 63 report
Lattice b	12.656 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 9 report
Lattice b	12.548 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 15 report
Lattice b	13.313 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 69 report
Lattice b	13.048 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 93 report
Lattice b	13.669 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 75 report
Lattice b	13.68 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 45 report
Lattice b	15.258 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 105 report
Lattice b	12.743 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 21 report
Lattice b	12.759 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 3 report
Lattice b	13.498 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 81 report
Lattice b	12.704 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 27 report
Lattice b	13.1 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 87 report
Lattice b	13.896 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 39 report
Lattice b	13.251 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 51 report
Lattice b	12.57 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 33 report
Lattice b	13.913 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 57 report
Lattice b	12.797 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 99 report
Lattice b	6.443 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 76 report
Lattice b	6.034 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 94 report
Lattice b	6.634 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 40 report
Lattice b	6.036 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 88 report
Lattice b	5.672 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 34 report
Lattice b	6.603 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 58 report
Lattice b	5.866 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 100 report
Lattice b	6.152 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 52 report
Lattice b	6.237 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 70 report
Lattice b	5.773 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 28 report
Lattice b	6.573 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 64 report
Lattice b	5.607 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 16 report
Lattice b	6.513 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 46 report
Lattice b	6.828 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 106 report
Lattice b	6.304 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 82 report
Lattice b	5.747 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 10 report
Lattice b	5.808 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 4 report
Lattice b	5.8 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 22 report
Lattice b	10.132 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 35 report
Lattice b	11.072 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 71 report
Lattice b	10.259 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 23 report
Lattice b	10.77 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 89 report
Lattice b	10.9 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 53 report
Lattice b	10.467 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 101 report
Lattice b	11.738 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 59 report
Lattice b	12.371 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 107 report
Lattice b	10.742 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 95 report
Lattice b	11.882 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 41 report
Lattice b	10.038 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 17 report
Lattice b	11.196 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 83 report
Lattice b	10.21 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 11 report
Lattice b	11.766 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 65 report
Lattice b	11.563 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 47 report
Lattice b	10.286 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 5 report
Lattice b	10.236 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 29 report
Lattice b	11.481 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 77 report
Lattice b	13.081 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 72 report
Lattice b	12.016 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 36 report
Lattice b	12.247 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 24 report
Lattice b	13.678 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 78 report
Lattice b	12.262 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 6 report
Lattice b	14.626 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 42 report
Lattice b	15.798 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 108 report
Lattice b	12.477 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 102 report
Lattice b	13.006 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 54 report
Lattice b	14.524 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 66 report
Lattice b	14.158 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 48 report
Lattice b	12.889 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 90 report
Lattice b	14.267 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 60 report
Lattice b	12.144 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 12 report
Lattice b	12.885 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 96 report
Lattice b	12.209 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 30 report
Lattice b	13.519 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 84 report
Lattice b	11.867 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 18 report
Lattice b	1.098 Å	298.15	(S) alloy: S 1	experimental	[2] Chen 2022 cites King 1981	Table I, p. 2, row 9 report
Lattice b	1.2866 Å	298.15	(αS) alloy: S 1	experimental	[3] Shi 2019 cites King 1981 doi	Table 2, p. 3, row 2 report
Lattice b	1.098 Å	298.15	(βS) alloy: S 1	experimental	[3] Shi 2019 cites Reid 2006 doi	Table 2, p. 3, row 3 report
Lattice b	7.641 Å	298.15	S.mP28	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 110 report
Lattice b	13.025 Å	298.15	S.mP32	experimental	[1] Hu 2010 cites Watanabe 1974 doi	Table A.2, p. 6, row 111 report
Lattice b	5.998 Å	298.15	S.mP56	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 112 report
Lattice b	10.96 Å	298.15	S.mP64	experimental	[1] Hu 2010 cites Sands 1965 doi	Table A.2, p. 6, row 113 report
Lattice b	12.866 Å	298.15	S.oF128	experimental	[1] Hu 2010 cites Rettig 1987 doi	Table A.2, p. 6, row 114 report
Lattice c	5.358 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 61 report
Lattice c	4.901 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 73 report
Lattice c	4.334 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 85 report
Lattice c	4.292 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 91 report
Lattice c	6.24 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 103 report
Lattice c	4.009 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 19 report
Lattice c	4.603 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 67 report
Lattice c	5.526 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 37 report
Lattice c	4.638 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 79 report
Lattice c	3.961 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 7 report
Lattice c	3.762 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 13 report
Lattice c	4.045 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 97 report
Lattice c	4.021 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 1 report
Lattice c	3.872 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 31 report
Lattice c	5.432 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 55 report
Lattice c	5.191 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 43 report
Lattice c	3.992 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 25 report
Lattice c	4.411 Å	0	S.hR6	DFT	[1] Hu 2010	Table A.2, p. 6, row 49 report
Lattice c	9.506 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 50 report
Lattice c	9.345 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 86 report
Lattice c	8.413 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 14 report
Lattice c	12.678 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 104 report
Lattice c	8.93 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 2 report
Lattice c	9.673 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 68 report
Lattice c	10.578 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 56 report
Lattice c	8.863 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 26 report
Lattice c	8.71 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 32 report
Lattice c	10.483 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 62 report
Lattice c	10.231 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 44 report
Lattice c	8.881 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 20 report
Lattice c	10.481 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 38 report
Lattice c	9.363 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 92 report
Lattice c	8.842 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 8 report
Lattice c	9.891 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 80 report
Lattice c	9.089 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 98 report
Lattice c	10.174 Å	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 74 report
Lattice c	10.684 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 63 report
Lattice c	8.527 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 9 report
Lattice c	8.184 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 15 report
Lattice c	9.553 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 69 report
Lattice c	9.302 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 93 report
Lattice c	10.134 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 75 report
Lattice c	10.502 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 45 report
Lattice c	13.321 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 105 report
Lattice c	8.637 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 21 report
Lattice c	8.654 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 3 report
Lattice c	9.752 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 81 report
Lattice c	8.584 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 27 report
Lattice c	9.384 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 87 report
Lattice c	10.894 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 39 report
Lattice c	9.374 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 51 report
Lattice c	8.375 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 33 report
Lattice c	10.835 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 57 report
Lattice c	8.816 Å	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 99 report
Lattice c	22.412 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 76 report
Lattice c	20.973 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 94 report
Lattice c	22.955 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 40 report
Lattice c	21.006 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 88 report
Lattice c	19.842 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 34 report
Lattice c	22.83 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 58 report
Lattice c	20.46 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 100 report
Lattice c	21.356 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 52 report
Lattice c	21.69 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 70 report
Lattice c	20.147 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 28 report
Lattice c	22.701 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 64 report
Lattice c	19.63 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 16 report
Lattice c	22.484 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 46 report
Lattice c	24.066 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 106 report
Lattice c	21.768 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 82 report
Lattice c	20.033 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 10 report
Lattice c	20.243 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 4 report
Lattice c	20.229 Å	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 22 report
Lattice c	10.008 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 35 report
Lattice c	11.122 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 71 report
Lattice c	10.259 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 23 report
Lattice c	10.775 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 89 report
Lattice c	10.935 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 53 report
Lattice c	10.424 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 101 report
Lattice c	11.98 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 59 report
Lattice c	12.961 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 107 report
Lattice c	10.796 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 95 report
Lattice c	12.118 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 41 report
Lattice c	9.813 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 17 report
Lattice c	11.224 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 83 report
Lattice c	10.146 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 11 report
Lattice c	11.984 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 65 report
Lattice c	11.753 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 47 report
Lattice c	10.268 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 5 report
Lattice c	10.201 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 29 report
Lattice c	11.627 Å	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 77 report
Lattice c	25.184 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 72 report
Lattice c	23.229 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 36 report
Lattice c	23.523 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 24 report
Lattice c	25.443 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 78 report
Lattice c	23.55 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 6 report
Lattice c	26.1 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 42 report
Lattice c	27.702 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 108 report
Lattice c	23.696 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 102 report
Lattice c	24.809 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 54 report
Lattice c	25.846 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 66 report
Lattice c	25.688 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 48 report
Lattice c	24.332 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 90 report
Lattice c	26.115 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 60 report
Lattice c	23.386 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 12 report
Lattice c	24.27 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 96 report
Lattice c	23.433 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 30 report
Lattice c	25.079 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 84 report
Lattice c	23.141 Å	0	S.oF128	DFT	[1] Hu 2010	Table A.2, p. 6, row 18 report
Lattice c	1.104 Å	298.15	(S) alloy: S 1	experimental	[2] Chen 2022 cites King 1981	Table I, p. 2, row 9 report
Lattice c	2.4486 Å	298.15	(αS) alloy: S 1	experimental	[3] Shi 2019 cites King 1981 doi	Table 2, p. 3, row 2 report
Lattice c	1.1104 Å	298.15	(βS) alloy: S 1	experimental	[3] Shi 2019 cites Reid 2006 doi	Table 2, p. 3, row 3 report
Lattice c	4.27 Å	298.15	S.hR6	experimental	[1] Hu 2010 cites Donnay 1955 doi	Table A.2, p. 6, row 109 report
Lattice c	9.409 Å	298.15	S.mP28	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 110 report
Lattice c	9.356 Å	298.15	S.mP32	experimental	[1] Hu 2010 cites Watanabe 1974 doi	Table A.2, p. 6, row 111 report
Lattice c	20.951 Å	298.15	S.mP56	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 112 report
Lattice c	10.9 Å	298.15	S.mP64	experimental	[1] Hu 2010 cites Sands 1965 doi	Table A.2, p. 6, row 113 report
Lattice c	24.486 Å	298.15	S.oF128	experimental	[1] Hu 2010 cites Rettig 1987 doi	Table A.2, p. 6, row 114 report
lattice beta	101.8 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 50 report
lattice beta	101.3 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 86 report
lattice beta	104.1 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 14 report
lattice beta	90 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 104 report
lattice beta	102.7 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 2 report
lattice beta	101.4 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 68 report
lattice beta	97.7 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 56 report
lattice beta	102.8 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 26 report
lattice beta	103.3 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 32 report
lattice beta	98.3 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 62 report
lattice beta	98.5 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 38 report
lattice beta	102.9 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 8 report
lattice beta	99.7 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 80 report
lattice beta	102.1 °	0	S.mP28	DFT	[1] Hu 2010	Table A.2, p. 6, row 98 report
lattice beta	126.6 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 63 report
lattice beta	123.7 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 9 report
lattice beta	123.1 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 15 report
lattice beta	124.8 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 69 report
lattice beta	124.6 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 93 report
lattice beta	126.2 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 75 report
lattice beta	126.4 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 45 report
lattice beta	129.7 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 105 report
lattice beta	123.9 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 21 report
lattice beta	126.1 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 81 report
lattice beta	124.9 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 87 report
lattice beta	126.8 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 39 report
lattice beta	123.6 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 33 report
lattice beta	127.1 °	0	S.mP32	DFT	[1] Hu 2010	Table A.2, p. 6, row 57 report
lattice beta	134 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 76 report
lattice beta	134.4 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 94 report
lattice beta	133.5 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 40 report
lattice beta	134.7 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 34 report
lattice beta	133.4 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 58 report
lattice beta	134.5 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 100 report
lattice beta	134.1 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 52 report
lattice beta	134.8 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 16 report
lattice beta	133.6 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 46 report
lattice beta	133.2 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 82 report
lattice beta	134.6 °	0	S.mP56	DFT	[1] Hu 2010	Table A.2, p. 6, row 10 report
lattice beta	94 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 35 report
lattice beta	96 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 71 report
lattice beta	94.9 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 23 report
lattice beta	95.7 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 89 report
lattice beta	95.8 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 53 report
lattice beta	94.6 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 101 report
lattice beta	98.3 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 59 report
lattice beta	100.7 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 107 report
lattice beta	98.7 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 41 report
lattice beta	93.3 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 17 report
lattice beta	96.5 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 83 report
lattice beta	94.3 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 11 report
lattice beta	98.1 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 65 report
lattice beta	97.9 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 47 report
lattice beta	94.8 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 5 report
lattice beta	97.3 °	0	S.mP64	DFT	[1] Hu 2010	Table A.2, p. 6, row 77 report
lattice beta	102.1 °	298.15	S.mP28	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 110 report
lattice beta	125 °	298.15	S.mP32	experimental	[1] Hu 2010 cites Watanabe 1974 doi	Table A.2, p. 6, row 111 report
lattice beta	133.9 °	298.15	S.mP56	experimental	[1] Hu 2010 cites Steudel 1980 doi	Table A.2, p. 6, row 112 report
lattice beta	96.7 °	298.15	S.mP64	experimental	[1] Hu 2010 cites Sands 1965 doi	Table A.2, p. 6, row 113 report
volume printed: Volume	25.76 Å3/atom		α-S	experimental	[4] Guan 2017 cites Rettig 1987 doi	Table 1, p. 5, row 1 report
volume printed: Volume	23.51 Å3/atom	0	α-S	DFT	[4] Guan 2017	Table 1, p. 5, row 3 report
volume printed: Volume	27.29 Å3/atom	0	α-S	DFT	[4] Guan 2017	Table 1, p. 5, row 2 report
volume printed: Volume	26.86 Å3/atom	0	δ-S	DFT	[4] Guan 2017	Table 1, p. 5, row 8 report
volume printed: Volume	22.2 Å3/atom	0	δ-S	DFT	[4] Guan 2017	Table 1, p. 5, row 9 report

Other property (5)

Other property, S system
Property	Value	T (K)	Phases / composition	Class	Source	Location
bulk modulus printed: B0	11.096 GPa (range 7.692 to 14.5)		α-S	experimental	[4] Guan 2017 cites Rettig 1987 doi	Table 1, p. 5, row 1 report
bulk modulus printed: B0	12.242 GPa	0	α-S	DFT	[4] Guan 2017	Table 1, p. 5, row 3 report
bulk modulus printed: B0	5.804 GPa	0	α-S	DFT	[4] Guan 2017	Table 1, p. 5, row 2 report
bulk modulus printed: B0	7.252 GPa	0	δ-S	DFT	[4] Guan 2017	Table 1, p. 5, row 8 report
bulk modulus printed: B0	9.349 GPa	0	δ-S	DFT	[4] Guan 2017	Table 1, p. 5, row 9 report

Sources

Reporting papers the values were read from (a value cited from another work names that work in its row).

Rongxiang Hu, Michael C. Gao, Ömer N. Doğan, Paul King, Michael Widom, Thermodynamic modeling of the Pd–S system supported by first-principles calculations, Calphad 34, 324-331 (2010). doi:10.1016/j.calphad.2010.07.002
Shanxiong Chen, Jiong Wang, Shangzhao Yu, Biao Hu, Qing Wu, Yong Du, Thermodynamic Modeling of the Ge-X (X = As, Se, S, P) Systems, J. Electron. Mater. 51, 2114-2130 (2022). doi:10.1007/s11664-022-09474-1
Chenying Shi, Biaobiao Yang, Biao Hu, Yong Du, Sheng Yao, Thermodynamic Description of the Al–X (X = S, Se, Te) Systems, J. Phase Equilib. Diffus. 40, 392-402 (2019). doi:10.1007/s11669-019-00733-z
Pin-Wen Guan, Shun-Li Shang, Greta Lindwall, Tim Anderson, Zi-Kui Liu, First-principles calculations and thermodynamic modeling of the S-Se system and implications for chalcogenide alloys, Journal of Alloys and Compounds 694, 510-521 (2017). doi:10.1016/j.jallcom.2016.10.037

Please cite

R. Arróyave, J. Saal, D. Shin, ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature (version 2026.10; Version 1, machine-extracted), Zenodo (2026). doi:10.5281/zenodo.23735569
R. Arróyave, J. Saal, D. Shin, ORCHID data: umbrella record of the ORCHID datasets (version 2026.10; Version 1, machine-extracted), Zenodo (2026). doi:10.5281/zenodo.23736065

Also cite the original source of every value you use (paper_citation / paper_doi, and cited_dois for values the paper cites from earlier work); B. Hallstedt, The SGTE collection of binary datasets, Calphad 89 (2025) 102833, https://doi.org/10.1016/j.calphad.2025.102833 (CC BY 4.0), and the original assessment named in each file; A. Jain et al., The Materials Project: A materials genome approach to accelerating materials innovation, APL Materials 1 (2013) 011002, https://doi.org/10.1063/1.4812323 (CC BY 4.0); J. E. Saal et al., JOM 65 (2013) 1501, https://doi.org/10.1007/s11837-013-0755-4 and S. Kirklin et al., npj Comput. Mater. 1 (2015) 15010, https://doi.org/10.1038/npjcompumats.2015.10 (CC BY 4.0). Version 1, machine-extracted: values were read by language-model readers constrained to quote their source and checked automatically, and the release was then audited on the printed pages by adversarial audits, an independent second review of fit-facing records and a preliminary human review of a frozen sample. Flags such as accepted and ESPEI-ready record screening results, not certification; known issues are listed in the release notes.

@misc{orchid_literature_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID-Values: thermodynamic and phase-equilibrium values read from the literature}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23735569},
  url       = {https://doi.org/10.5281/zenodo.23735569},
  note      = {Version 1, machine-extracted}
}

@misc{orchid_data_2026,
  author    = {Arr{\'o}yave, Raymundo and Saal, James and Shin, Dongwon},
  title     = {{ORCHID data: umbrella record of the ORCHID datasets}},
  version   = {2026.10},
  publisher = {Zenodo},
  year      = {2026},
  doi       = {10.5281/zenodo.23736065},
  url       = {https://doi.org/10.5281/zenodo.23736065},
  note      = {Version 1, machine-extracted}
}